研究二次冷轧压下率对于硅的质量分数为3.0%的无取向硅钢组织结构和磁性能的影响。结果表明：当第二次冷轧压下率从0变化至16.7%时,铁损逐渐增加,磁感逐渐降低。当第二次冷轧压下率大于16.7%时,随压下率的增加,铁损逐渐减小,磁感逐渐增加。当第二次冷轧压下率大于38%时,二次冷轧法所能获得的磁性能明显优于一次冷轧法。
Effect of double cold reduction on magnetic,microstructure and texture of 3.0% Si non-oriented silicon steel sheets was investigated.The results show that the iron loss increases and magnetic induction reduces as the percentage redcution in secondary cold rolling changes from 0 to 16.7%.The core loss can be reduced remarkably,and magnetic induction can get a little benefit if the percentage redcution in double cold reduction is higher 16.7%.In case of higher than 38% of the percentage redcution in secondary cold rolling,the improvement of the magnetic properties is even more than one rolled.
参考文献
| [1] | 何忠志.电工钢[M].北京:冶金工业出版社,1997 |
| [2] | 毛卫民;张新明.晶体材料织构定量分析[M].北京:冶金工业出版社,1995 |
| [3] | 金自力,徐向棋.轧制条件对冷轧无取向硅钢织构的影响[J].特殊钢,2005(02):25-27. |
| [4] | Tomida T;Tarakal T .Development of(100)Texture in Sili con Steel Sheets by Removel of Manganese and Decarburization[J].ISIJ International,1995,35(05):548. |
| [5] | Sidor Y;Dzubinsky M;Kovac F .Characterization of Micro-structures in Non-Oriented Electrical Steels Utilizing Weighted Sum of Elementary Data[J].Czechoslovak Journal of Physics,2004,54:105. |
| [6] | Takashima M.;Morito N.;Komatsubara M. .(001)(210) TEXTURE DEVELOPMENT BY TWO-STAGE COLD ROLLING METHOD IN NON-ORIENTED ELECTRICAL STEEL[J].ISIJ International,1997(12):1263-1268. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%