The warm compression tests were performed on the eutectoid steel to investigate the evolution of cementite morphology. Several processing parameters, such as temperature, strain rate and reduction, were changed to analyze the effect of each parameter on spheroidization of cementite. The results showed that the warm compression promoted the fragmentize and the spheroidization of lamellar cementites. When the specimen was compressed with reduction of 50% at 700 ℃ and in the strain rate of 0.01 s-1, the excellent spheroidized cementite was obtained. The mechanism of fragmentation and spheroidization of lamellar cementites during compression was discussed by using transmission electron microscope. The formation of spheroidized cementite was related to the time of compression process. The fragmentize of lamellar cementites was due to the extension of sub-grain boundary in the cementite. The spheroidization of cementite depended on the diffusion of carbon atoms at the tip of bended and breakup cementite.
参考文献
| [1] | |
| [2] | . Harrigan, M.J. and O.D. Sherby, Kinetics of spheroidization of a eutectoid composition steel as influenced by concurrent straining. Materials Science and Engineering, 1971. 7(4): p. 177-189.2. Karadeniz, E., Influence of different initial microstructure on the process of spheroidization in cold forging. Materials & Design, 2008. 29(1): p. 251-256.3. Wang, B., X. Song, and H. Peng, Design of a spheroidization processing for ultrahigh carbon steels containing Al. Materials & Design, 2007. 28(2): p. 562-568.4. Lesuer, D.R., C.K. Syn, and O.D. Sherby, Fracture behavior of spheroidized hypereutectoid steels. Acta Metallurgica et Materialia, 1995. 43(10): p. 3827-3835.5. Di, H., et al., Spheroidizing kinetics of eutectic carbide in the twin roll-casting of M2 high-speed steel. Journal of Materials Processing Technology, 2005. 166(3): p. 359-363.6. Z.T.Wang, T.D.G., Theory of Metal Plastic Forming. 2nd edn. 1989. Machine press, Beijing: p. 30-43.7. Yanagida, A. and J. Yanagimoto, A novel approach to determine the kinetics for dynamic recrystallization by using the flow curve. Journal of Materials Processing Technology, 2004. 151(1-3): p. 33-38.8. H.G.Read, W.T.R., APFIM and TEM studies of drawn pearlitic wire. Scripta Materialia, 1997(37): p. 1221-1230.9. Languillaume, J., G. Kapelski, and B. Baudelet, Evolution of the tensile strength in heavily cold drawn and annealed pearlitic steel wires. Materials Letters, 1997. 33(3-4): p. 241-245.10. Danoix, F., et al., Direct evidence of cementite dissolution in drawn pearlitic steels observed by tomographic atom probe. Materials Science and Engineering A, 1998. 250(1): p. 8-13.11. K.Hono, M.O., M.Murayama, S.Nishida, A.Yoshie, T.Takahashi, Cementite decomposition in heavily drawn pearlite steel wire. Scripta Materialia, 2001(44): p. 977-983.12. Porter, L.F. and P.C. Rosenthal, Effect of applied tensile stress on phase transformations in steel. Acta Metallurgica, 1959. 7(7): p. 504-514.13. P.M.Umemoto, H.O., I.Tamura., Transformation from work-hardened austenite. Transactions ISIJ, 1983(23): p. 775.14. B.Champagne, M.B., R.Angers, Metallography of boron carbide. Metallography, 1976(9): p. 357-359. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%