通过两相区退火和贝氏体转变区等温处理,研究了铌含量和贝氏体等温处理温度对低碳 TRIP钢(w(Mn)=1.38%,w(Si)=0.6%,w(Al)=0.5%)组织和力学性能的影响.实验结果表明:增加铌含量,实验钢的残余奥氏体量减少,抗拉强度和屈服强度增加;当铌的质量分数为0.014%时,实验钢的伸长率和强塑积较高;贝氏体等温处理温度为400 ℃时,实验钢的残余奥氏体量较多,力学性能较好.
参考文献
[1] | Ushilda K .Rencent Developments in Steel Sheets[J].Scandinavian Journal of Metallurgy,1999,28(01):33-39. |
[2] | Girault E;Jacques P;Harlet P .Metallographic Methods for Revealing the Multiphase Microstructure of TRIP-Assisted Ateels[J].Materials Characterization,1998,40(02):111-118. |
[3] | Ray A;Dhua S K .Microstructural Manifestations in Color:Some Applications for Steels[J].Materials Characterization,1996,37(01):1-8. |
[4] | Matsumura O .Retained Austenite in 0.4C-Si-1.2Mn Steel Sheet Intercritically Heated and Austempered[J].ISIJ International,1992,32(09):1014-1020. |
[5] | Lee C G;Kim S J;Song B H et al.Effect of Heat Treatment on Formability in 0.15C-1.5Si-1.5Mn Multiphase Cold-Rolled Steel Sheet[J].Metals and Meterials International,2002,8(05):435-441. |
[6] | Pichler A .TRIP Steels With Reduced Si Content[J].Steel Research International,1999,70(11):459-465. |
[7] | M. De MEYER .The Influence of the Substitution of Si by Al on the Properties ofCold Rolled C-Mn-Si TRIP Steels[J].ISIJ International,1999(8):813-822. |
[8] | W. Bleck;A. Frehn;E. Kechagias .Control of microstructure in TRIP steels by niobium[J].Materials Science Forum,2003(Pt.1):43-48. |
[9] | Matsuda Hiroshi;Kitano Fusato;Hasegawa Kohei .Metallurgy of continuously annealed high strength TRIP steel sheet[J].Steel Research,2002(6/7):211-217. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%