为了提高Fe-Al金属间化合物涂层的结合强度和耐磨性,改善其室温韧性,研制了一种新型FeAlCr电弧喷涂粉芯丝材,利用高速电弧喷涂技术在45#钢基体表面制备了涂层.采用扫描电镜(SEM)、能谱仪(EDAX)和X射线衍射仪分析了涂层的微观结构和微区成分,用显微硬度计、拉伸试验机和CETR微动摩擦磨损试验机等试验设备对涂层的力学性能进行了分析.结果表明,喷涂FeAlCr粉芯丝材过程中合金元素反应充分,涂层组织均匀、致密,氧化物含量极低.主要相组成有Fe-Al、Ni3Al金属间化合物,硬质相Cr3C2、氧化物Cr2O3和Al2O3弥散分布在韧性相α-Fe基体上.涂层平均HV显微硬度为5.50 GPa,约是基体的2倍,平均结合强度约47.2MPa,载荷100 N油润滑条件下涂层的耐磨性高于基体,磨损率随着摩擦过程的进行呈降低趋势.
参考文献
| [1] | Elmasides C.;Verykios XE. .Mechanistic study of partial oxidation of methane to synthesis gas over modified Ru/TiO2 catalyst[J].Journal of Catalysis,2001(2):477-486. |
| [2] | Lee HY;Jung SH;Lee SY;Ko KH .Alloying of cold-sprayed Al-Ni composite coatings by post-annealing[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(7):3496-3502. |
| [3] | Srivastava AK.;Dhar A.;Gupta AK.;Anandani RC. .Effect of thermal conditions on microstructural features during spray forming[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2001(0):587-591. |
| [4] | 张忠礼,李德元,张楠楠.电弧喷涂铝青铜涂层的力学性能[J].表面技术,2006(02):10-12. |
| [5] | 雷阿利,李高宏,冯拉俊,徐大鹏.过渡材料对等离子喷涂Al2O3梯度陶瓷涂层性能影响[J].焊接学报,2007(10):25-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%