以聚碳酸亚丙酯二醇、二苯基甲烷二异氰酸酯(MDI)和1,4-丁二醇(BDO)等为原料,采用预聚体法合成了聚碳酸亚丙酯聚氨酯弹性体(PUE-PPC).研究表明,PUE-PPC拉伸强度和撕裂强度优于聚醚型弹性体;与聚酯型弹性体相比,具有较好的水解稳定性,经35 d浸泡后,其拉伸强度保持率高出33％.研究了异氰酸酯指数(R)、预聚体-NCO基含量、扩链剂种类等对PUE-PPC力学性能的影响.结果表明,随着R值减小,弹性体的拉伸强度和撕裂强度先增大后减小,并在R=1.05时达到最大值,断裂伸长率则一直增大;随着-NCO基含量的增加,弹性体的拉伸强度和撕裂强度提高,而断裂伸长率减小;扩链剂链长越短,弹性体力学性能越好.
参考文献
| [1] | 刘保华,张敏,陈立班.脂肪族聚碳酸酯聚氨酯的合成研究进展[J].聚氨酯工业,2002(04):6-9. |
| [2] | Robertson NJ;Qin ZQ;Dallinger GC;Lobkovsky EB;Lee S;Coates GW .Two-dimensional double metal cyanide complexes: highly active catalysts for the homopolymerization of propylene oxide and copolymerization of propylene oxide and carbon dioxide[J].Dalton transactions: An international journal of inorganic chemistry,2006(45):5390-5395. |
| [3] | Xu SP;Zhang M .Synthesis and characterization of a novel polyurethane elastomer based on CO2 copolymer[J].Journal of Applied Polymer Science,2007(6):3818-3826. |
| [4] | 王东山,余爱芳,何树杰,杨淑英,陈立班.聚碳酸亚丙酯聚氨酯的合成与性能[J].高分子学报,1999(02):162-166. |
| [5] | Jimenez G.;Shishido A.;Sumita M.;Asai S. .Effect of the soft segment on the fatigue behavior of segmented polyurethanes[J].European Polymer Journal,2000(9):2039-2050. |
| [6] | 张晓华,曹亚.软段对IPDI基透明聚氨酯弹性体微相结构与性能的影响[J].中国塑料,2005(08):27-31. |
| [7] | 谢富春,张玉清,朱长春,牛杰峰.二醇扩链剂对聚醚聚氨酯弹性体性能的影响[J].粘接,2006(03):4-5,8. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%