采用以硫酸镍为主盐的电沉积技术,在MB8形变镁合金表面制备纳米复合镀层.利用扫描电镜和透射电镜观察复合镀层的显微形貌和微观结构,利用X射线衍射仪和能谱仪对复合镀层进行物相分析,利用显微硬度计测定镀层显微硬度,利用快速磨损试验机测试复合镀层的耐磨性能,利用电化学测试仪测定复合镀层在3.5%NaCl(质量分数)溶液中的极化曲线.结果表明:在MB8形变镁合金表面可以获得结晶均匀、结构致密的纳米复合镀层,该复合镀层的显微硬度最高达HV 682,其耐磨性能超过硬铬镀层,且具有较好的耐蚀性能,自腐蚀电位较镁合金基体提高677 mV.
参考文献
| [1] | 张新明,陈健美,邓运来,肖阳,蒋浩.Mg-Gd-Y-Zr耐热镁合金的压缩变形行为[J].中国有色金属学报,2005(12):1925-1932. |
| [2] | ANYANWU I A;KAMADO S;KOJIMA Y .Creep properties of Mg-Gd-Y-Zr alloy[J].Materials Transactions,2001,42(01):1212-1218. |
| [3] | LUO ALAN A .Recent magnesium alloy development for automotive power train application[J].Materials Science Forum,2003,419-422(01):56-57. |
| [4] | DRITS M E;SVIDERKAYA Z A;ROKHLIN L L .Effect of alloying on properties of Mg-Gd alloys[J].Metallovcdenici Termicheskaya,1979,11:62-64. |
| [5] | GUANG L S;ANDRFJ A .The electrochemical corrosion of pure magnesium in 1 N NaCI[J].Corrosion Science,1997,39(05):855-875. |
| [6] | 孙颖,李燕青,魏晓伟,慕东.镁合金表面防护研究进展[J].四川工业学院学报,2004(04):4-5,9. |
| [7] | 霍宏伟,李瑛,王福会.AZ91D镁合金化学镀镍[J].中国腐蚀与防护学报,2002(01):14-17. |
| [8] | 胡文彬,向阳辉,刘新宽,刘磊,丁文江.镁合金化学镀镍预处理过程表面状况的研究[J].中国腐蚀与防护学报,2001(06):340-344. |
| [9] | Maria Lekka;Niki Kouloumbi;Mauro Gajo;Pier Luigi Bonora .Corrosion and wear resistant electrodeposited composite coatings[J].Electrochimica Acta,2005(23):4551-4556. |
| [10] | Kuo SL;Chen YC;Ger MD;Hwu WH .Nano-particles dispersion effect on Ni/Al2O3 composite coatings[J].Materials Chemistry and Physics,2004(1):5-10. |
| [11] | 郭鹤桐;张三元.复合镀层[M].天津:天津大学出版社,1991 |
| [12] | 李瑛,余刚,刘跃龙,叶立元,郭小华,雷细平.镁合金上硫酸镍体系化学镀镍工艺[J].材料保护,2003(10):32-34. |
| [13] | 李光玉,牛丽媛,江中浩,孙丽萍,连建设.电流密度对纳米锌镍合金镀层显微组织的影响[J].吉林大学学报（工学版）,2006(06):835-840. |
| [14] | LEKKA M;KOULOUMBI N;GAJO M;BONORA P L .Corrosion and wear resistant eioctrodeposited composite coatings[J].Electrochemical Acta,2005,50:4551-4556. |
| [15] | W.X. Zhang;N. Huang;J.G. He;Z.H. Jiang;Q. Jiang;J.S. Lian .Electroless deposition of Ni-W-P coating on AZ91D magnesium alloy[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2007(11):5116-5121. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%