利用聚苯乙烯微球模板,采用负压抽滤注浆工艺制备了羟基磷灰石(hydroxylapatite,HA)内连通空心球陶瓷支架,分析了制备工艺对空心球陶瓷的形貌特征和力学性能的影响,并研究了孔隙率与压缩强度的关系.结果表明,空心球陶瓷支架具有连通球形孔及连通球体间隙的独特复合孔结构;当注浆2次,浆料固含量为0.5g/ml时支架的孔壁完整,表面形态有利于骨细胞生长;通过改变工艺参数,得到HA空心球陶瓷的孔隙率为61%~90%,压缩强度为1.1~6.9MPa,孔隙率P与压缩强度σf的关系符合ln(σf)=ln(σf0)-bP方程.
参考文献
[1] | Burg K J L;Porter S;Kellam J F .[J].BIOMATERIALS,2000,21:47-59. |
[2] | Vacant C A;Bonassar L J .[J].Clinical Orthopaedics,1999,367(S):375-381. |
[3] | TakafumiY;Hajime O .[J].Biomedical Materials & Engineering,1998,8(03):311-320. |
[4] | Thijs I;Luyten J;Mullens S .[J].Journal of the American Ceramic Society,2003,87(01):170-172. |
[5] | Del R R P;Wolke J G C;Vallet R M .[J].Biomaterials,2002,23:3673-3680. |
[6] | Nam YS;Park TG .Porous biodegradable polymeric scaffolds prepared by thermally induced phase separation.[J].Journal of biomedical materials research, Part B. Applied biomaterials,1999(1):8-17. |
[7] | 和峰,刘昌胜.添加成孔剂法制备孔径、气孔率可控的多孔玻璃陶瓷[J].无机材料学报,2004(06):1267-1276. |
[8] | 方丽茹,翁文剑,沈鸽,韩高荣,Santos JD,杜丕一.骨组织工程支架及生物材料研究[J].生物医学工程学杂志,2003(01):148-152. |
[9] | 罗德福,赵康,陈永楠,马楚凡,吴少旭.内部连接的球形多孔羟基磷灰石支架的制备[J].硅酸盐学报,2007(03):368-372. |
[10] | 罗德福,赵康,苏波,吴少旭.球形多孔羟基磷灰石支架的孔结构特征与力学性能[J].硅酸盐学报,2007(09):1205-1209. |
[11] | Liu D M .[J].Journal of Materials Science Letters,1996,15(02):419-421. |
[12] | Hench L L;Wilson J.An Introduction to Bioceramics[M].Singapore:World Scientific Publishing Co.Ptc.Ltd,1993:24-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%