采用差示扫描量热法(DSC)和热重分析法(TGA)研究了一种含铱配合物的新型共聚物PVKIr的热性能.结果表明,该聚合物的玻璃化转变温度(Tg)为220.04℃,起始分解温度(Td)为454.31℃,具有良好的热稳定性.利用该聚合物为发光材料制备了电致发光器件ITO/聚(3,4.乙撑二氧噻吩)(PEDOT)(45 nm)/2-(4-联苯基)-5-(4-叔丁基苯基)-1,3,4-噁二唑(PBD):25%PVKIr(80 nm)/2,9-二甲基-4,7-二苯基-1,10-菲咯啉(BCP)(15 nm)/三(8-羟基喹啉)铝(Alq3)(30 nm)/LiF(1 nm)/Al,其最大发射峰在532 nm,起亮电压为13 V.该器件在驱动电压为21 V时,达到最大亮度86cd/m2,而此时电流密度为192 mm/cm2.
参考文献
| [1] | J. Kalinowski .Optical materials for organic light-emitting devices[J].Optical materials,2008(5):792-799. |
| [2] | 徐清,刘羡春,侯琳熙,肖通虎.新型含铱共聚物的合成及表征[J].功能材料,2009(11):1780-1782,1786. |
| [3] | Ling QD;Cai QJ;Kang ET;Neoh KG;Zhu FR;Huang W .Monochromatic light-emitting copolymers of N-vinylcarbazole and Eu-complexed 4-vinylbenzoate and their single layer high luminance PLEDs[J].Journal of Materials Chemistry: An Interdisciplinary Journal dealing with Synthesis, Structures, Properties and Applications of Materials, Particulary Those Associated with Advanced Technology,2004(18):2741-2748. |
| [4] | 吴江勇,吴志兵,陈浩,李瑛,李龙章,蒋青.新型主链含方酸菁的低能隙烷基芴共聚物的合成及性质[J].高分子材料科学与工程,2007(05):33-36. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%