采用粉末冶金真空烧结方法制备了Ti(C, N)/NiCr金属陶瓷.研究了TiN含量对Ti(C, N)/NiCr金属陶瓷微观结构与力学性能的影响. 结果表明，TiN的加入既改变了金属陶瓷硬质相颗粒的尺寸，使其变小，也改变了硬质相颗粒的形貌，使其由圆形变为多边形；随TiN含量的增加，金属陶瓷的抗弯强度均出现先增加后降低的规律，但在较低的烧结温度下，抗弯强度在TiN含量为4%时达到最大值，而在较高的烧结温度下，抗弯强度在TiN含量为6%时达到最大值；硬度在TiN含量<＝10%时变化不明显，TiN含量>10%时硬度急剧下降；抗弯断口以穿晶解理为主要的断裂模式.
Ti(C,N)/NiCr cermets were vacuum sintered by powder metallurgy technology. The effects of TiN additions on microstructures and mechanical properties of Ti(C, N)/NiCr cermets were investigated. Results revealed that the hard phase particles were refined and the morphology of the particles changed from a circular to a polygonal shape by the additions of TiN because of the formation of Ti(C,N) solid solution; With increasing TiN additions, the bonding strength increased to the maximum values at 4%TiN content during low sintering temperature and at 6%TiN content during high sintering temperature, respectively, and then decreased. Hardness changed little when TiN addition was less than 10%, but decreased dramatically when TiN addition exceeded 10%. Fracture photograph showed that trans-granular fracture was the main failure mode because of the good interface bonding strength between binding phase and ceramic hard phase.
参考文献
| [1] | |
| [2] | |
| [3] | |
| [4] | |
| [5] | |
| [6] | |
| [7] | |
| [8] | |
| [9] | |
| [10] | |
| [11] | |
| [12] | |
| [13] | |
| [14] | |
| [15] | |
| [16] |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%