Effect of the heat treatment, including solution treatment (ST) and aging treatment (AT), on the prior austenite grain (PAG) size, microstructure and mechanical properties of a precipitation hardening maraging stainless steel was investigated. The results indicate that the relations between PAG size and yield strength (σy) under both ST and AT conditions obey the Hall-Petch relationship. Furthermore, after ST at 1050℃for 1 h+cryogenic treated (CT) at -70℃ for 8 h+AT at 535℃ for 4 h, the tested steel showed its ultimate tensile strength (σb) and σy over 1900 MPa and 1750 MPa, respectively.
参考文献
| [1] | L D Wang;L H Jiang;M Zhu;X Liu and W M Zhou .[J].Journal of Materials Science and Technology,2004,20(02):217. |
| [2] | Liuding WANG,Laizhu JIANG,Ming ZHU,Xiao LIU,Wangmin ZHOU.Improvement of Toughness of Ultrahigh Strength Steel Aermet 100[J].材料科学技术学报（英文版）,2005(05):710-714. |
| [3] | M.M.A.Gad,H.G.Salem,A.M.Nasreldin,H.Sabry,A.A.El-sayed.Localized Corrosion Behavior of 6% Mo Super Austenitic ＆ 316L Stainless Steels in Low pH 3% NaCl Solution[J].材料科学技术学报（英文版）,2005(04):465-469. |
| [4] | D R Askeland;P P Phulé.Essentials of Materials Science and Engineering[M].北京:清华大学出版社,2005:402. |
| [5] | Y. He;K. Yang;W. -S. Qu .Effects of solution treatment temperature on grain growth and mechanical properties of high strength 18 percent Ni cobalt free maraging steel[J].Materials Science and Technology: MST: A publication of the Institute of Metals,2003(1):117-124. |
| [6] | 何毅,杨柯,孔凡亚,曲文生,苏国跃.超高强度18Ni无钴马氏体时效钢的力学性能[J].金属学报,2002(03):278-282. |
| [7] | H C Holm;M Bichsel;P Uggowitzer .[J].Script Metallurgical,1984,18:373. |
| [8] | Y He;K Yang;W S Qu;F Y Kong and G Y Su .[J].Materials Letters,2002,56:763. |
| [9] | D Webster .[J].Transactions ASM,1968,61:816. |
| [10] | R. TEWARI;S. MAZUMDER;I. S. BATRA .PRECIPITATION IN 18 WT Ni MARAGING STEEL OF GRADE 350[J].Acta materialia,2000(5):1187-1200. |
| [11] | A Hitit .[D].Carnegie Mellon University,Pittsburgh,Pennsylvania,2002. |
| [12] | G P Miller;W I Mitchell .[J].Journal of the Iron and Steel Institute,1965,9:899. |
| [13] | G W Tuffnell;R L Cairns .[J].Transactions ASM,1968,61:798. |
| [14] | Y Kawabe;K Nakazawa;S Muneki .[J].Tetsu To Hagane-Journal of The Iron and Steel Institute of Japan,1976,62:1229. |
| [15] | H J Rack .[J].Materials Science and Engineering,1978,34:263. |
| [16] | S Floreen;R F Decker .[J].Transactions ASM,1962,55:518. |
| [17] | C.N.Hsiao;C.S.Chiou;J.R.Yang .Aging reactions in 17-4 PH stainless steel[J].Materials Chemistry and Physics,2002(2):134-142. |
| [18] | H R H Bajguirani .[J].Materials Science and Engineering A,2002,338:142. |
| [19] | D L Corn;A R Wazzan .[J].Journal of the Iron and Steel Institute,1968,6:600. |
| [20] | B P Kashyap;K Tangri .[J].Materials Science and Engineering A,1992,149:L13. |
| [21] | K T Tharian;D Sivakmar;R Ganesan;P Balakrishnan and P P Sinha .[J].Materials Science and Technology,1991,7:1082. |
| [22] | W Sha;A Cerezo;G D W Smith .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1993,24:1251. |
| [23] | E. V. Pereloma;A. Shekhter;M. K. Miller .Ageing behaviour of an Fe-20Ni-l.8Mn-l.6Ti-0.59Al (wt percent) maraging alloy: clustering, precipitation and hardening[J].Acta materialia,2004(19):5589-5602. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%