使用溶胶凝胶法和有机泡沫浸渍工艺制备了(45-x)CaO-xLa2O3-4.5MgO-33SiO2-16P205-0.5CaF2(0≤x≤5)(质量分数)体系的多孔生物活性玻璃陶瓷.研究了不同含量的氧化镧对材料的晶相组成、力学强度、生物活性、磁性和生物相容性的影响.研究结果表明,La2o3的掺入量x≤5时,提高了生物活性玻璃陶瓷的力学强度,赋予了材料一定的磁性能,但当掺入量为x=5时,对材料的生物相容性造成了一定的影响.
参考文献
| [1] | Arcos D;del RR;Vallet Regi M .A novel bioactive and magnetic biphasic material.[J].Biomaterials,2002(10):2151-2158. |
| [2] | Bretcanu O;Spriano S;Vitale CB;Verne E .Synthesis and characterization of coprecipitation-derived ferrimagnetic glass-ceramic[J].Journal of Materials Science,2006(4):1029-1037. |
| [3] | Kokubo T.A/W Glass-ceramic:Processing and Properties.Bioceramic World Scientific[M].Singapore:World Scientific Publishing Co.Ptc.Ltd,1993:75. |
| [4] | 郭伯生.稀土在生物领域中应用研究进展[J].稀土,1999(01):64. |
| [5] | Xue M;Ou J;ZhouD L et al.[J].Key Engineering Materials,2007,330-332:169. |
| [6] | Kokubo T;Kushitani H;Sakka S et al.[J].Journal of Biomedical Materials Research,1990,24:721. |
| [7] | Kokubo T .[J].J Non Cryst Solias,1990,120:136. |
| [8] | 温波,黄颖,徐勇忠.氧化钛生物陶瓷骨细胞相容性研究[J].吉林大学学报(医学版),2004(03):418-419,424. |
| [9] | Ttheodora L;Kis A C;Korey S et al.[J].Materials Research Society,2002,711:271. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%