The electrical conductivity of pure CaTiO3 and that containing 0.5 similar to5.0 mole fraction CuO as dopant were measured in the temperature range 291 similar to 773 K. The conductivity values varied as a function of temperature and dopant concentration. The activation energy in the lower temperature range depended on the impurity content while in the high temperature range it indicated a value of energy gap width. The infrared absorption spectra in the range of 100 similar to 4000 cm(-1) revealed the presence of two main bands at 340 and 570 cm(-1) which were assigned to TiO6 octahedral normal mode. Bands in the range of 106 similar to 270 cm(-1) were due to the vibration of anion TiO3-2. Some bands were observed at higher values due to the presence of lattice imperfections. There was a slight shift in band position with increasing dopant concentration which favors the formation of orthorhombic modification.