应用电容测试法并借助于点缺陷模型(PDM)计算了2205双相不锈钢与316L奥氏体不锈钢在NaCl溶液中所形成的钝化膜内点缺陷的扩散系数,利用实验测得钝化膜的稳态电流和PDM模型对计算结果进行了验证分析.通过两种计算方法得到点缺陷在2205双相不锈钢与316L奥氏体不锈钢钝化膜内的扩散系数约为10-23cm2/s～10-20cm2/s数量级,并发现在模拟海水溶液中2205钢的扩散系数比316L钢小,氧空位所形成的点缺陷在2205钢的钝化膜内比316L钢扩散困难,从而使得2205不锈钢的钝化膜比316L不锈钢更加致密与完整,保护性能更好.
参考文献
| [1] | Elzbieta Sikora;Digby D. Macdonald .Nature of the passive film on nickel[J].Electrochimica Acta,2002(1):69-77. |
| [2] | 李党国,冯耀荣,白真权,郑茂盛.X80管线钢钝化膜内点缺陷扩散系数的计算[J].应用化学,2008(09):1007-1010. |
| [3] | Cheng YF.;Yang C.;Luo JL. .Determination of the diffusivity of point defects in passive films on carbon steel[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2002(1/2):169-173. |
| [4] | Ahn S;Kwon H .Diffusivity of point defects in the passive film on Fe[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,2005(2):311-319. |
| [5] | 李金波,郑茂盛,朱杰武.304L不锈钢钝化膜半导体性能研究[J].腐蚀科学与防护技术,2006(05):348-352. |
| [6] | 程学群,李晓刚,杜翠薇.316L和2205不锈钢在醋酸溶液中钝化膜的生长及其半导体属性的研究[J].科学通报,2009(01):104-109. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%