对超声表面波在电解充氢430不锈钢中的传播特性进行了试验,使用ABWML-4ST-90°表面波探头、PCI卡采集超声波数据,利用公式得到衰减系数,并测定了充氢前后材料的显微硬度.结果表明:随着电解充氢过程的不断进行,超声表面波衰减系数显著增大,波速显著降低,与钢中氢浓度趋近于线性关系;当材料表面的氢浓度达到饱和后,衰减系数和波速也趋于恒定;不锈钢发生氢蚀后显微硬度出现了明显的下降.
参考文献
| [1] | Liu XB;Takamori S;Osawa Y .Effect of matrix structure on ultrasonic attenuation of ductile cast iron[J].Journal of Materials Science,2007(1):179-184. |
| [2] | Lei Zhang;Shihua Tang;Hongliang Pan .Study on the Relationship of Hydrogen Content and Ultrasonic Propagation Properties[J].Key engineering materials,2007(4):2549-2552. |
| [3] | 李萍,李喜孟,谭家隆,王来.超声检测技术用于评价20钢高温组织转变[J].中国测试技术,2006(01):11-13. |
| [4] | K.Y. Chin;F.T. Cheng;H.C. Man .Hydrogen effect on the cavitation erosion resistance of AISI 316L stainless steel laser surface-modified with NiTi[J].Materials Letters,2007(26):239-243. |
| [5] | Ellina Lunarska;Danuta Samatowicz .The hydrogen-induced modification of the properties of the metal surface coated with oil and lubricant[J].Tribology International,2000(7):491-499. |
| [6] | 董志勇,胡金榜.超声波衰减系数法评估材料损伤的研究[J].化工机械,2007(03):139-143. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%