采用全自动控制往复喷射成形工艺制备了φ360 mm×1200 mm工业规格7475铝合金喷射成形坯.采用常规力学性能和电导率测试,应用光学显微镜、扫描电镜和透射电镜观察微观组织,研究了沉积态、挤压态和热处理状态下喷射成形7475铝合金组织和性能的演变.结果表明,沉积态组织为等轴晶,粒度宏观均匀,晶粒尺寸在30 ～ 40 μm,无明显宏观偏析,致密度达97％,强度比传统铸造合金提高63.6％;热挤压后,孔隙基本消除,比传统铸造合金强度提高45.5％,伸长率提高25.3％.T6处理后,强度为738 MPa,电导率为39.4％IACS,比传统铸造合金强度提高33.0％,电导率提高9.4％;双级时效降低合金强度,提高电导率;回归再时效处理后,强度为716 MPa,电导率达43.3％IACS,能使合金获得优异的综合性能.
参考文献
| [1] | 郑祥健,李浩言,李勇,王岩.固溶处理对7475铝合金组织和性能的影响[J].轻合金加工技术,2004(08):45-47,51. |
| [2] | Mala M. Sharma .Microstructural and mechanical characterization of various modified 7XXX series spray formed alloys[J].Materials Characterization,2008(1):91-99. |
| [3] | Sitdikov O;Sakai T;Miura H et al.Temperature effect on fine-grained structure formation in high-strength A1 alloy 7475 during hot severe deformation[J].Materials Science and Engineering A,2009,516(1/2):180-188. |
| [4] | Ren, SR;Ma, ZY;Chen, LQ .Effect of initial butt surface on tensile properties and fracture behavior of friction stir welded Al-Zn-Mg-Cu alloy[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2008(1/2):293-299. |
| [5] | Wang Feng;Xiong Baiqing;Zhang Yongan;Liu Hongwei;Li Zhihui;Liu Qiang .Microstructure and mechanical properties of spray-deposited Al–Zn–Mg–Cu alloy processed through hot rolling and heat treatment[J].Materials Science & Engineering. A, Structural Materials: Properties, Misrostructure and Processing,2009(1/2):144-149. |
| [6] | 张君尧.我国铝材应用的进展及今后发展(1)[J].轻金属,1994(02):58-62. |
| [7] | 张君尧.我国铝材应用的进展及今后发展(2)[J].轻金属,1994(04):60-64. |
| [8] | Grant P S .Spray forming[J].Progress in Materials science,1995,39(4/5):497-545. |
| [9] | Jenabali Jahromi S A .Creep behavior of spray-cast 7XXX aluminum alloy[J].Materials and Design,2002,23(02):169-172. |
| [10] | 李红英,程勇胜,郑子樵.时效制度对7475铝合金挤压件组织与性能的影响[J].中南工业大学学报(自然科学版),2001(04):394-397. |
| [11] | 李铁.7475合金挤压棒材生产工艺探索[J].铝加工,2004(04):52-54. |
| [12] | 于帆,吴晓锋,齐艳.7475铝合金扁锭熔铸工艺研究[J].轻合金加工技术,2007(05):9-12. |
| [13] | 张福全,乔志伟,陈振华,张辉.微量液相与7475铝合金的超塑性变形[J].矿冶工程,2007(04):71-73. |
| [14] | 肖亚庆;谢水生;刘静安.铝加工技术使用手册[M].北京:冶金工业出版社,2005 |
| [15] | 尹志民,方家芳,黄继武,聂波,单长智,郭加林,王琳.时效工艺对7A52铝合金晶间腐蚀和剥蚀行为的影响[J].中南大学学报（自然科学版）,2007(04):617-622. |
| [16] | 段水亮,刘志义,段安静,周杰.双级时效对7475铝合金组织与性能的影响[J].金属热处理,2008(08):112-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%