Effect of cryogenic treatment on the microstructure, hardening behavior and abrasion resistance of 14Cr2Mn2V high chromium cast iron (HCCI) subjected to subcritical treatment was investigated. The results show that cryogenic treatment after subcritical treatment can obviously improve the hardness and abrasion resistance of HCCI because abundant retained austenite is transformed into martensite and fine secondary carbides [(Fe, Cr)23C6] precipitate. The amount of martensite and precipitated secondary carbide in HCCI experiencing subcritical treatment followed by cryogenic treatment was more than that experiencing the subcritical treatment followed by air cooling. When the abrasion resistance of HCCI reaches the maximum, its microstructure contains about 15% retained austenite. Cryogenic treatment can further reduce the austenite content but the retained austenite cannot be transformed into martensite completely.
参考文献
| [1] | Tabrett C P;Sare I R .The Effect of Heat Treatment on the Abrasion Resistance of Alloy White Iron[J].Wear,1997,203-204:206-219. |
| [2] | SUN Zhi-ping;ZUO Ru-lin;LI Cong .TEM Study on Precipitation and Transformation of Secondary Carbides in 16Cr-1Mo-1Cu White Iron Subjected to Subcritical Treatment[J].Materials Characterization,2004,53:403-409. |
| [3] | J T H Pearce .High Chromium Cast Irons to Resist Abrasive Wear[J].Foundryman,2002(4):156-166. |
| [4] | Zhiping Sun;Rulin Zuo;Cong Li .Relations of abrasion resistance and hardness of 16Cr-3C white irons with retained austenite content[J].Journal of University of Science and Technology Beijing,2004(6):539-544. |
| [5] | C. P. Tabrett;I. R. Sare .Effect of high temperature and sub-ambient treatments on the matrix structure and abrasion resistance of a high-chromium white iron[J].Scripta materialia,1998(12):1747-1753. |
| [6] | C. P. Tabrett;I. R. Sare;M. R. Ghomashchi .Microstructure-property relationships in high chromium white iron alloys[J].International Materials Reviews,1996(2):59-82. |
| [7] | 王均,孙志平,刘浩怀,高升吉,沈保罗,黄四九.一种高铬铸铁亚临界处理的硬化动力学研究[J].铸造,2003(11):1065-1068. |
| [8] | D. Mohan Lal;S. Renganarayanan;A. Kalanidhi .Cryogenic treatment to augment wear resistance of tool and die steels[J].Cryogenics,2001(3):149-155. |
| [9] | A. Molinari;M. Pellizzari;S. Gialanella .Effect of deep cryogenic treatment on the mechanical properties of tool steels[J].Journal of Materials Processing Technology,2001(1/3):350-355. |
| [10] | DONG Yun;LIN Xiao-ping;XIAO Hong-shen .Deep Cryogenic Treatment of High Speed Steels and Its Mechanism[J].Heat Treatment of Metals,1998,3:55-61. |
| [11] | J.Y. Huang;Y.T. Zhu;X.Z. Liao .Microstructure of cryogenic treated M2 tool steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2003(1/2):241-244. |
| [12] | Sinatora A;Pohl M;Waldherr E U .Wear Induced Martensite in High Chromium Cast Iron[J].Scripta Materialia,1995,32:857-861. |
| [13] | XU Li-qun;Vose C;St John D .Abrasive Wear Study of Selected White Cast Irons as Liner Materials for the Mining Industry[J].Wear,1993,162-164:820-832. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%