采用一步法制备了表面接枝甲基丙烯酰氧基三甲氧基硅烷(MPS)的单分散SiO2胶体球,并通过垂直沉积法在40℃、60%相对湿度下组装出有序性较好的密排结构的SiO2光子晶体.傅立叶红外光谱(FT-IR)和X射线光电子能谱(XPS)结果证明SiO2胶体球表面接枝上了MPS;扫描电子显微镜(SEM)结果表明改性后SiO2胶体球平均粒径为284nm,单分散性较高,平均标准偏差＜5%;制备出的光子晶体是面心立方(fcc)紧密堆积结构;吸收光谱表明,所制备的光子晶体在(111)方向具有光子晶体的带隙特性,带隙中心波长为646nm.
参考文献
| [1] | Yablonovitch E .[J].Physical Review Letters,1987,58:2059-2062. |
| [2] | John S .[J].Physical Review Letters,1987,58:2486-2489. |
| [3] | Li J;Herman P R;Valdivia C E et al.[J].Optics Express,2005,13:6454-6459. |
| [4] | Ben-Moshe M;Alexeev V L;Asher et al.[J].Chemistry-A European Journal,2006,78:5149-5157. |
| [5] | Sinitskii AS;Knot'ko AV;Tretyakov YD .Silica photonic crystals: synthesis and optical properties[J].Solid state ionics,2004(1/4):477-479. |
| [6] | Masahiko I;Hiroshi N;Hideyuki N et al.[J].Langmuir,2005,21:5367-5371. |
| [7] | Chung Y W;Lee J H;Hon M H et al.[J].Applied Physics A,2004,79:2089-2092. |
| [8] | Yoshinaga K.;Chiyoda M.;Ishiki H.;Okubo T. .Colloidal crystallization of monodisperse and polymer-modified colloidal silica in organic solvents[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2002(1/3):285-293. |
| [9] | Wang W;Gu B H;Liang L Y et al.[J].Journal of Physical Chemistry B,2003,107:12113-12117. |
| [10] | 吉小利,王君,李爱元,徐国财.纳米二氧化硅粉体的表面改性研究[J].安徽理工大学学报(自然科学版),2004(z1):83-87. |
| [11] | Tolani G;Csempesz F;Kabai-Faix M et al.[J].Langmuir,2001,17:2683-2687. |
| [12] | 毋伟,陈建峰,邵磊,初广文.聚合物接枝改性超细二氧化硅表面状况及形成机理[J].北京化工大学学报(自然科学版),2003(02):1-4. |
| [13] | Woodcock L V .[J].Nature,1997,385:141-143. |
| [14] | FANG Jun;WANG XiuFeng;WANG LieSong;CHENG Bing;WU YuanTing;ZHU WanLin .Preparation of modified SiO_2 colloidal spheres with succinic acid and the assembly of colloidal crystals[J].Chinese science bulletin,2007(4):461-466. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%