采用湿混工艺，经冷压、烧结、复压后制备了添加碳化钒的新型银镍石墨电触头材料，利用扫描电镜和光学显微镜观察了材料的显微组织，并对材料的性能进行了测试。结果表明：所制备的新型银镍石墨材料的相对密度达98．2％，硬度和电导率分别为903MPa和45．0％IACS，组织均匀，断口韧窝较细小，电寿命次数达10145次，与传统银镍石墨电触头材料相比有了显著提高。
The new-style AgNiC electrical contact material was fabricated by wet blending, die pressing, sintering and repressing process. The microstructure was observed by scan electron microscopy and optical microscopy, and the properties were tested. The results show that the relative density of the new-type AgNiC could reach 98. 2%, and the hardness and electrical conductivity was 903 MPa and 45.0%IACS respectively. The homogeneous microstructure and finer fracture dimple were obtained. The electrical life time of the new-type AgNiC was 10 145 cycle times which was much better than the traditional one.
参考文献
| [1] | 钱宝光,耿浩然,郭忠全,杨勤达,陶珍东.电触头材料的研究进展与应用[J].机械工程材料,2004(03):7-9. |
| [2] | 郭自鹏,董亮,王豫.银基金属氧化物电触头材料的发展与现状[J].电工材料,2007(02):35-39. |
| [3] | 余海峰,雷景轩,马学鸣,朱丽慧,陆尧,项兢.新型AgC5电触头材料的性能及显微组织[J].稀有金属材料与工程,2004(01):96-100. |
| [4] | 马学鸣,雷景轩.制粉工艺对制备银/石墨电触头材料性能的影响[J].热处理,2003(01):24-27. |
| [5] | 李恒,侯月宾.AgNi系列触头材料在直流灯负载下的电侵蚀特点[J].电工材料,2005(03):12-14,25. |
| [6] | 罗群芳,刘丽琴,王亚平,丁秉钧.机械合金化方法制备银镍触头合金的研究[J].稀有金属材料与工程,2003(04):298-300. |
| [7] | 吴春萍,陈敬超,周晓龙,李玉华,鲜春桥.银基电接触材料[J].云南冶金,2005(01):46-51. |
| [8] | 马荣骏.银基电接触材料研究与应用的进展[J].稀有金属与硬质合金,2008(04):28-36. |
| [9] | 贾志华,马光,王轶,郑晶.稀土在银基接触材料中的作用与应用[J].材料开发与应用,2008(06):76-81,84. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%