研究了不同热处理工艺下Ni53Mn23.5Ga21.5Ti2铁磁性形状记忆合金的显微结构和相变行为.利用SEM、TEM、DSC和XRD等考察了Ni53Mn23.5Ga21.5Ti2合金中热处理制度对马氏体相变和组织结构的影响.结果表明:Ni53Mn23.5Ga21.5Ti2合金经1273 K,5 h热处理时有序度最高,呈单相结构.合金经1123 K,24 h热处理后在晶内和晶界上弥散分布着大量的析出相.经1473 K,5 h热处理时合金有序度很低,说明此时合金部分或全部熔化.在不同的热处理制度下合金的晶体结构并不改变,仍呈现5M的马氏体晶体结构.
参考文献
| [1] | O'Handley A D;Murray R C;Marioni S J et al.[J].Applied Physics,2000,87(09):4712. |
| [2] | Ullakko K;Huang J K;Kantner C et al.[J].Applied Physics Letters,1996,69(13):1966. |
| [3] | Wu G H;Yu C H;Meng L Q et al.[J].Applied Physics Letters,1999,75(19):2990. |
| [4] | Wang W H;Wu G H;Chen J L et al.[J].Applied Physics Letters,2000,77(20):3245. |
| [5] | Liu J;Zheng H X;Xia M X et al.[J].Scripta Materialia,2005,52:955. |
| [6] | Nishida M;Wayman C M;Kainuma R et al.[J].Scripta Metallurgica,1986,20:899. |
| [7] | Schryvers D;Tirry W;Yang Z Q.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006(438-440):485. |
| [8] | 王文洪,柳祝红,陈京兰,吴光恒,梁婷,徐惠彬,蔡伟,郑玉峰,赵连城.铁磁形状记忆合金Ni52.5Mn23.5Ga24马氏体相变热滞后的研究[J].物理学报,2002(03):635-639. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%