通过扫描和能谱分析及温度场模拟对350mm×470mm轴承钢连铸坯内部裂纹进行了研究.结果表明:裂纹处存在一定的夹杂物,夹杂物主要是Al2O3、MgO及部分铝硅酸盐,其中Al2O3夹杂物较大,长度达70μm,宽度为40μm左右;夹杂物主要是由于在炉外精炼中使用了高碱度和较高Al2O3含量的渣系,生产过程中卷渣等造成的;在连铸过程中,液固两相区存在夹杂物,成为裂纹源,铸坯固液界面所承受的应力及由此产生的塑性变形超过了所允许的高温强度和临界应变值,沿夹杂物方向扩展形成裂纹.
参考文献
| [1] | Brimacombe J K .Empowerment With Knowledge-Toward the Intelligent Mold for the Continuous Casting of Steel Billets[J].Metallurgical and Materials Transactions,1993,24B(06):917. |
| [2] | Won Y. M.;Yeo T.-J. .A New Criterion for Internal Crack Formation in Continuously Cast Steels[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(4):779-794. |
| [3] | 逯洲威.薄板坯连铸工艺液芯压下的有限元分析[J].上海金属,2002(05):17-20. |
| [4] | Zhiqiang HAN;Kaike CAI;Baicheng LIU .Prediction and Analysis on Formation of Internal Cracks in Continuously Cast Slabs by Mathematical Models[J].ISIJ International,2001(12):1473-1480. |
| [5] | Hawbolt E B;Weinberg F;Brimacombe J K .Influence of HotWorking on Internal Cracks in Continuously-Cast Steel Billets[J].Metallurgical and Materials Transactions,1979,10B(02):229. |
| [6] | Erica Fuchs;Par Jonsson .Inclusion Characteristics in Bearing Steel Before and During Ingot Casting[J].HIGH TEMPERATURE MATERIALS AND PROCESSES,2000(5):333-344. |
| [7] | M. Goransson;F. Reinholdsson;K. Willman .Evaluation of liquid steel samples for the determination of microinclusion characteristics by spark-induced optical emission spectroscopy[J].Iron & Steelmaker,1999(5):53-58. |
| [8] | 高海潮.钢中氢、氮、氧的来源及其控制对策[J].炼钢,2000(02):38-43,53. |
| [9] | Uesugi T .Recent Development of Bearing Steel in Japan[J].Tetsu To Hagane-Journal of the Iron & Steel Institute of Japan,1988,74(10):1889. |
| [10] | Kawakami K;Taniguchi T;Nakashima K .Generation Mr chanisms of Non-Metallic Inclusions in High-Cleanliness Steel[J].Tetsu To Hagane-Journal of the Iron & Steel Institute of Japan,2007,93(12):743. |
| [11] | L.Zhang;S.Taniguchi .Fluid Flow and Inclusion Removal in Continuous Casting Tundish[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2000(2):253-266. |
| [12] | Cremer P;Driole J .Effects of the Electromagnetic Stirring on the Removal of Inclusions of Oxide From Liquid Steel[J].Metallurgical and Materials Transactions,1982,13B(01):45. |
| [13] | 祭程,朱苗勇,曹学欠,赵忠义,赵贺朝,赵丽华,李海龙.高碳合金钢连铸动态轻压下工艺控制技术的研究与应用[C].第七届中国钢铁年会论文集,2009:1545-1550. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%