使用钛酸丁酯作为前驱体,在聚偏氟乙烯-六氟丙烯溶液中分解为TiO2,与聚合物基体进行复合,制备的聚合物膜吸附电解质溶液后成为微孔复合聚合物电解质(MCPE).用SEM、DSC、FT-IR、XRD等方法对复合聚合物膜进行表征,并测试了MCPE的离子电导率,发现当复合聚合物膜中TiO2粒子的质量分数为8.2%时,聚合物电解质具有最高的离子电导率1.27×10-3S/cm.
参考文献
| [1] | Gozdz A S;Schmutz C N;Tarascon J M .[P].US 5296138,1994. |
| [2] | Kwang M K;Nam-Gyu P;Kwang S R et al.[J].POLYMER,2002,43(14):3951-3957. |
| [3] | Caillon C M;Claude M B;Lemordant D et al.[J].Journal of Power Sources,2002,107(01):125-132. |
| [4] | 杜宏伟,孔瑛.PI/TiO2纳米复合材料的耐溶剂和耐热性能研究[J].高分子学报,2003(02):288-292. |
| [5] | Teyssedre G;Bernes A;Lacabanne C .[J].J Polym Sci B,1993,31:2027-2034. |
| [6] | Martin S;Stephan S;Ralf B W et al.[J].Macromolecules,2003,36(10):3646-3651. |
| [7] | Salimi A.;Yousefi AA. .FTIR studies of beta-phase crystal formation in stretched PVDF films[J].Polymer Testing,2003(6):699-704. |
| [8] | Rajendran S;Mahendran O;Mahalinga T .[J].European J Polymer,2002,38:49-55. |
| [9] | Martin S;Stephan S;Ralf B W et al.[J].Macromolecules,2003,36(10):3646-3651. |
| [10] | 陈国荣,史鹏飞,白永平,范太炳.新型复合聚合物电解质离子导电行为的研究[J].化学学报,2004(04):377-380. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%