通过恒温拉伸试验测定了10CrNi3MoV钢在室温至1 000℃温度范围内的延伸率和强度,并借助热膨胀法测定了试验钢的相变特征温度Ac1和Ac3.结果表明,10CrNi3MoV钢在720~750℃温度区间内断后延伸率超过100%,表现出超塑性行为;其中720℃时塑性最好,断后延伸率达到123.5%,该温度略高于Ac1温度.
参考文献
[1] | 胡正寰;夏巨谌.中国材料工程大典第21卷[M].北京:化学工业出版社,2006:344-345. |
[2] | 吴诗傲.金属超塑性变形理论[M].北京:国防工业出版社,1997:3-4. |
[3] | Sherby O D;Walser B;Young C M.Superphstic ultrahigh carbon steels[J].Scripta Metall,1975(09):569-574. |
[4] | Tomita Y;Okabayashi K.Improvement in lower temperature mechanical properties of 0.40 pct C-Ni-CrMo ultrahigh strength steel with the second phase lower bainite[J].Metallurgical Transactions,1983(14A):485-492. |
[5] | Tomita Y;Okabayashi K.Heat treatment for improvement in lower temperature mechanical properties of 0.40 pct C-Cr-Mo ultrahigh strength steel[J].Metallurgical Transactions,1983(14A):2387-2393. |
[6] | Speis H J;Frommeyer G.Superplasticity behaviour of rapidly solidified ultrahigh carbon tool steel X380CrVMo2593[J].Materials Science and Tethnology,1991(07):718-722. |
[7] | Sato E.Microstructure control for suprrplasticity of an uhrn-high ccarbou sterf[J].Materials Science Forum,1999:304-306. |
[8] | C.-R. Xu;W. Gao;Y.-L. Yang .Superplastic boronizing of a low alloy steel - microstructural aspects[J].Journal of Materials Processing Technology,2001(3):349-355. |
[9] | 张寒,白秉哲.一种实现低合金超高强钢超塑变形的新思路[J].热处理,2012(02):24-27. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%