为抑制碱性锌酸盐体系锌-铁合金电镀中氢气的析出,提高阴极电流效率,在分析铁族金属原子结构的基础上,筛选得到了性能优良的负二价硫族化合物抑氢剂.研究了该抑氢剂对锌-铁合金电镀的阴极电流效率及电化学行为的影响.结果表明:抑氢剂对纯锌电镀阴极电流效率的影响很小,基本上保持在80%左右;加入抑氢剂可使锌-铁合金共沉积的阴极电流效率由未加抑氢剂时的63.28%提高到83.54%;抑氢剂的最佳用量为20mL/L.
参考文献
| [1] | FKATESI R;ROVENTI G;GIULIANI G et al.Zino-cobalt alloy electrodeposition from chloride baths[J].Journal of Applied Electrochemistry,1997,27(09):1088-1094. |
| [2] | Y. Liao;D. R. Gabe;G. D. Wilcox .A study of zinc-iron alloy electrodeposition using a rotating cylinder hull cell[J].Plating & Surface Finishing,1998(3):60-66. |
| [3] | PAATSCH W;KAUTEK W;SAHRE M .Corrosion behaviour and mechanical properties of plated Zn-alloys[J].Transactions of the lnstitate of Metal Finishing,1997,75(06):216-218. |
| [4] | SHORT N R;DENNIS J K .Corrosion resistance of zinc-alloy coated steel in construction industry environments[J].Transactions of the Institute of Metal Finishing,1997,75(02):47-52. |
| [5] | BIKULCIUS G .Control of thicknOSS of corrosion-resistant Zn-Fe,Zn-Co & Zn-Ni coatings[J].Plating and Surface Finishing,1997,84(08):30-32. |
| [6] | 王云燕,彭文杰.锌酸盐镀锌阴极电流效率的研究[J].电镀与环保,2003(06):12-16. |
| [7] | 王云燕,彭文杰.锌酸盐体系Zn-Fe合金电镀阴极电流效率的研究[J].材料保护,2004(05):16-18. |
| [8] | 王云燕,彭文杰,柴立元,舒余德.碱性锌酸盐电镀Zn-Fe合金工艺的研究[J].电镀与环保,2003(02):11-14. |
| [9] | 王云燕,彭文杰,柴立元,舒余德.Electrochemical behaviors of Zn-Fe alloy and Zn-Fe-TiO2 composite electrodeposition[J].中南工业大学学报(英文版),2003(03):183-189. |
| [10] | 张允诚;胡如南;向荣.电镀手册[M].北京:国防工业出版社,1997:95-154. |
| [11] | 屠振密.电镀合金原理与工艺[M].北京:国防工业出版社,1993:231-243. |
| [12] | 舒余德;陈白珍.冶金电化学研究方法[M].长沙:中南工业大学出版社,1990:159-162. |
| [13] | 查全性.电极过程动力学导论[M].北京:科学出版社,1987:407-415. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%