借助压实曲线、X射线衍射等分析手段,研究了膨滑土、NaOH溶液等粘结剂对玻璃配合料的压实性的影响,并对其粘结机理进行了分析.研究结果表明:粘结剂的加入能有效提高玻璃配合料的致密化程度,最小致密化临界压力值仅为8 kN.玻璃配合料的压实性与粘结剂的加入量密切相关,在相同条件下,随着粘结剂加入量的增加,配合料的压实性提高,致密化临界压力值降低.同时,压实曲线的变化趋势也与粘结剂的加入量有关,在不同的粘结剂加入量下,配合料的压实曲线存在很大差异.
参考文献
| [1] | 刘建安 .粒化料在玻璃窑炉中的应用[J].山东轻工业学院学报,1994,8(03):54-56. |
| [2] | Kalygin V G;Nazarov V I;Chekhov O S.Chemical-exchange reactions during the compaction of glass batches[J].Slate Scientific-Research Institute of Glass,1986(02):47-50. |
| [3] | N. S. Krasheninnlkova;I. V. Frolova;O. V. Kaz'mina .A METHOD FOR PREPARING HOMOGENEOUS GLASS BATCH[J].Glass and ceramics,2004(5/6):173-174. |
| [4] | V. E. Manevich;K. Yu. Subbotin;V. D. Tokarev .Physicochemical Processes in Transportation and Storage of Glass Batch[J].Glass and ceramics,2003(11/12):353-355. |
| [5] | Kalygin V G;Nazarov V I;Chekov O S.Compaction of batch for flat glass[J].State Scientific -Research Institute of Glass,1985(03):121-124. |
| [6] | 赵忠恕.石英细砂球团化用于玻璃原料分析[J].中国玻璃,2004(06):7-9. |
| [7] | 蔡启南.玻璃配合料球团化的发展概况[J].玻璃,1982(01):25-28. |
| [8] | 陈建民;童月珍;耿海棠.玻璃配合料压块熔化新工艺中间试验[J].玻璃,1984(04):1-6. |
| [9] | Kalygin V G;Nazarov V I;Chekov O S.Chemical-exchange reactions during the compaction of glas batches[J].State Scientific-Research Institute of Glass,1986(02):47-50. |
| [10] | 马毅杰 .膨润土资源、性质及其利用[J].土壤学进展,1994,22:21-28. |
| [11] | 邱俊,张言贵,李静静,吕宪俊.利用膨润土制备无机凝胶的机理和工艺研究[J].山东科技大学学报（自然科学版）,2007(01):42-44. |
| [12] | 刘德汞,曹书勤.珍珠岩高温碱溶制取水玻璃[J].信阳师范学院学报(自然科学版),2003(01):68-69,72. |
| [13] | Krasheninnikova N S;Frolova I V;Vereshchagin V I.Application of granulated raw concentrate in glass technology[J].Class and Ceramics,2004 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%