高纯原料的制备是制造高品质光纤最重要的环节，本文采用氯气氛下水平区熔法生长单晶的提纯方法对卤化银原料进行超提纯．区域熔融提纯后的卤化银原料红外吸收光谱测量显示在800～4000cm－1范围内吸收随波长的增加而降低．经CO2激光量热计法测量提纯后的卤化银原料在10．6μm处的吸收系数为5×10－4Cm－1，较提纯前降低两个数量级，制成的光纤传输损耗03～0．5dB／m
The preparation of high purity raw materials is the foremost section in fabrication of high quality optical fibers. The material of silver halide was ultrapurified by horizontal zone
melting purification in Cl2 atmosphere. Measurement results show that infrared absorbance will decrease as wavenumber increases at 800～4000cm-1
after the ultrapurification, and the absorption coefficient of silver halide preform crystal by CO2 laser calorimeter is less than 5×10-4cm-1
at 10.6μm. The absorption coefficient decreases two order of magnitude after ultrapurification. The optical fiber loss is 0.3～0.5 dB/m.
参考文献
| [1] | Paiss I, et al. SPIE “Infrared Fiber Optics III”, 1991, 1591: 70--82. [2] Paiss I, et al. SPIE “Optical Fibers in Medicine”, 1991, 1420: 141--148. [3] Moser F, et al SPIE “Infrared Fiber Optics II”, 1990, 1228: 128--139. [4] 阙端麟. 材料科学技术百科全书. 北京: 中国大百科全书出版社, 1995. 97--99. [5] Kebn-ichi Takahashi, et al. SPIE “Infrared Optical Materialand Fibers V?”, 1987, 843: 143--148. [6] 杨启基. 材料科学技术百科全书. 北京: 中国大百科全书出版社, 1995. 849--850. [7] 罗梓贤. 材料科学技术百科全书. 北京: 中国大百科全书出版社, 1995. 959--960. [8] 天津大学等. 有机化学. 北京: 人民教育出版社, 1978. 455--464. [9] Bunimovich D, et al. Applied Optics, 1994, 33 (1): 117--119. |