通过硬度测试、拉伸性能测试、X射线衍射分析和显微组织观察等方法研究了时效处理对锻态OAll0-5-5铝青铜组织和性能的影响。结果表明：锻态QA0-5-5铝青铜较好的时效处理工艺为650℃×2h；在此工艺下，合金的硬度、抗拉强度、屈服强度、伸长率分别为212HB，769MPa，492MPa和18．23％，与锻态合金的相比分别提高了8．16％，6．22％，12．33％和13．94％；经650℃×2h时效后，基体α相和（α＋γ2）共析体组织分布均匀，合金中均匀析出了较多细颗粒状的κ相并弥散分布。
Influences of aging treatment on microstructure and properties of forged QAll0-5-5 aluminum bronze were studied by hardness test, tensile test, X-ray diffraction analysis, microstructure observation. The results show that the aged QAll0 5-5 aluminum bronze exhibited fairly good mechanical properties when aging condition was 650 ℃×2 b. Under this aging condition, the hardness, tensile strength, yield strength and elongation of the aged alloy were 212 HB, 769 MPa, 492 MPa and 18.2% respectively, which were improved by 8. 16G, 6.22%, 12. 33% and 13. 94% respectively compared with those of the forged alloy, and more fine granular phase precipitated from alloy diffused well in the homogeneously distributed mierostructure of matrix of α-phase and (α+γ2)euteetoid.
参考文献
| [1] | 周志明,谷成渝,牟飞,梁隆.高强度铝青铜合金的研究进展[J].热加工工艺,2010(07):41-44. |
| [2] | 张卫文,夏伟,温利平,吴苑标,潘国如.Mechanical properties and tribological behavior of a cast heat-resisting copper based alloy[J].中南工业大学学报(英文版),2002(04):235-239. |
| [3] | 张大童,陈瑞萍,罗宗强,张卫文,李元元.热处理温度对高强变形铝青铜的组织和力学性能的影响[J].稀有金属,2010(04):521-525. |
| [4] | 何勇.QAl10-5-5铝青铜热处理工艺的研究[J].国外金属热处理,2005(02):12-15,18. |
| [5] | 张卫文,倪东惠,夏伟,邱诚,陈维平.Influence of heat treatment on tribological behaviors of novel wrought aluminum bronze[J].中国有色金属学会会刊(英文版),2002(04):770-774. |
| [6] | 宋练鹏,尹志民,冯然,徐应红.热处理对Cu-Al-Fe-Ni-Cr-RE合金组织和性能的影响[J].电力机车技术,2002(04):8-10. |
| [7] | 徐国富 .高速列车异步牵引电动机转子铜合金护环的研制[D].中南工业大学,2000. |
| [8] | 王荣滨.铝青铜热处理强化工艺试验研究[J].五金科技,2006(05):35-37. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%