以普通La2O3,硝酸,聚乙二醇为原料,利用溶胶-凝胶法制备了纳米La2O3粉体,利用TG-DTA,XRD,TEM等各种测试方法对干凝胶300℃灼烧所得前驱体粉末的分解过程及最终形成的纳米氧化镧粉体进行了分析和表征,并研究了浓度、搅拌和分散剂聚乙二醇(PEG)添加量等因素的改变对La2O3粉体的粒径、形态的影响.实验结果表明,在适当工艺参数下,可以制得平均粒径小于50 nm的La2O3粉体.
参考文献
| [1] | X.T.DONG.Preparation and properties of rare earth hydroxides and oxides ultrafine powders in alcohol[J].Chinese Chemical Letters,1995(11):1017. |
| [2] | 董相廷,刘桂霞,孙晶,李建利,刘景和,洪广言.Yb2O3纳米晶的制备及其若干性质的研究[J].稀有金属材料与工程,2001(01):73-76. |
| [3] | H. Vidal;S. Bernal;R. T. Baker;D. Finol;J. A. Perez Omil;J. M. Pintado;J. M. Rodriguez-Izquierdo .Characterization of La_2O_3/SiO_2 Mixed Oxide Catalyst Supports[J].Journal of Catalysis,1999(1):53-62. |
| [4] | Bernal S;Calvino J J et al.Nanostructural Evolution of High Loading Rh/lanthana Catalysts Through the Preparation and Reduction Steps[J].Catalysis Today,1999,52:29-43. |
| [5] | 王金淑,周美玲,左铁镛,张久兴,聂祚仁,胡延槽.La2O3对Mo粉性能影响的研究[J].稀有金属材料与工程,2002(02):140-143. |
| [6] | Buxbaum C;Gessinger G .Lanthanated Thermionic Cathodes[P].US 4083811,1978. |
| [7] | Goebel D M .La-Mo Emitter in Hollow Cathode[J].Review of Scientific Instruments,1980,51(11):1468-1470. |
| [8] | 王金淑,周美玲,张久兴,聂祚仁,左铁镛.碳化La2O3-Mo阴极材料的高温XPS研究[J].稀有金属材料与工程,2000(04):225-227. |
| [9] | 张纪光;马林;徐燕 .The Preparation and Characterization of Ultrafine Lanthanum Oxide by a Sol-Gel Process[J].复旦大学学报(自然科学版),1999,38(01):24-28. |
| [10] | 张梅,杨绪杰,陆路德,汪信.La2O3纳米晶的制备与表征[J].宇航材料工艺,1999(05):38-40. |
| [11] | 丁绪淮;谈遒.工业结昌[M].北京:化学工业出版社,1985 |
| [12] | 曹茂盛.超微颗粒制备科学与技术[M].哈尔滨:哈尔滨工业大学出版社,1998 |
| [13] | 胡维杰.结晶过程[M].大连:大连理工大学出版社,1991 |
| [14] | 翁培;周志朝;李中和.结晶学[M].北京:中国建筑工业出版社,1986 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%