通过对掺杂钨精矿粉末的Fe40Al60粉末压坯进行激光点燃自蔓延烧结,制备原位自生颗粒增强复合材料.利用表征手段分析钨精矿粉末添加量对烧结合金显微组织结构及宏观性能的影响规律.结果表明,随钨精矿粉含量的增加,合金显微组织由片状变为颗粒状,烧结合金物相主要为A12O3、FeAl、Fe3Al、Fe7W6、W及硬质颗粒相WO3.当钨精矿粉末含量为1％时,烧结合金密度最大,为4.27 g/cm3;孔隙率最小,为12.2％;硬度最高,上表层区达到1050 HV,中部区达到1818 HV,底层区达到1232 HV;合金磨损率最低,表层区为0.99 mg/mm2,中部区为0.59 mg/mm2,底层区为0.75 mg/mm2;合金耐蚀性能最好,腐蚀电流密度为116 μA/cm2.
参考文献
| [1] | 康新婷;杨坤;王建 等.Fe-Al金属间化合物抗氧化性能研究现状[J].稀有金属材料与工程,2012,41(09):822-826. |
| [2] | Pint BA;Zhang Y;Walker LR;Wright IG .Long-term performance of aluminide coatings on Fe-base alloys[J].Surface & Coatings Technology,2007(4/7):637-642. |
| [3] | Lakshmi J;Vendra;Afsaneh Rabiei .A study on aluminum-stell composite metal foam processed by casting[J].MATERIALS SCIENCE & ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2007,465(1-2):59-67. |
| [4] | Zhang L M;Liu B W;Sun D B .Preparation and properties of the Ni-Al/Fe-Al intermetallies composite coating produced by plasma cladding[J].International Journal of Minerals Metallurgy and Materials,2011,18(06):725-730. |
| [5] | Yeo I D;Ra T Y;Kim H S .Effect of Mo and Zr on microstructure,mechanical properties and wear resistance of Fe-A1 based alloys[J].Materials Science Technology,2008,24(03):309-312. |
| [6] | 刘俊友,刘杰,邹敦叙,张艺,景旭冉.21.4wt%Al的铁铝基金属间化合物1250℃的抗氧化性能[J].材料热处理学报,2009(05):26-29. |
| [7] | 张勇刚;韩雅芳;陈国良.金属间化合物结构材料(第1版)[M].北京:国防工业出版社,2001 |
| [8] | 孙康宁;尹衍升;李爱民.金属间化合物/陶瓷基复合材料(第1版)[M].北京:机械工业出版社,2002 |
| [9] | 李刚,陈永君,水东莉,唐海鹏,刘丽,侯俊英.高能激光束引燃Fe-Al系合金的制备与性能研究[J].材料热处理学报,2011(04):17-20. |
| [10] | 迟丽娜,王存山,庞宏杰,张凯舒.成分对激光诱导自蔓延反应合成Ti-Fe合金组织性能影响[J].材料热处理学报,2007(03):22-25. |
| [11] | 李刚,于君娜.钨精矿粉掺杂Fe-Al合金激光引燃自蔓延合金组织及性能[J].复合材料学报,2013(02):132-136. |
| [12] | 洪雨,吴玉程,李云,汪峰涛,王庆平,李东辉.添加钨和稀土元素对TiAl合金性能的影响[J].合肥工业大学学报（自然科学版）,2009(11):1707-1710. |
| [13] | 李婷婷,彭超群,王日初,王小锋,刘兵,王志勇.Fe-Al、Ti-Al和Ni-Al系金属间化合物多孔材料的研究进展[J].中国有色金属学报,2011(04):784-795. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%