采用热压烧结制备了ZrO2(3Y)/Fe3Al复合材料,材料的室温抗弯强度、断裂韧性、HRA硬度分别为1321MPa、36MPa·m1/2、86.7,临界热震温差(ΔT)由单相ZrO2(3Y)的250℃提高至500℃.显微结构研究表明,裂纹桥联、裂纹偏转及相变增韧的协同作用,及位错对裂纹扩展的扰动作用是断裂韧性成倍增加的主要原因.
ZrO2(3Y)/Fe3 Al composites were synthesized by HP sintering.The results show that their room flexural strength,fracture toughness and hardness(HRA)measured are 1321MPa, 36MPa·m1/2 and 86.7 respectively,and their critical temperature difierence(ΔT)of thermal shock elevates from 250℃ of ZrO2(3Y)to 500℃.The elevation of fracture toughness results from the compatible effect of crack bridge,crack deflection,stress-induced transformation toughening and the disturbing of dislocation on crack spread.
参考文献
| [1] | ] Klassen T, Günther R, Dickau B. J. Am. Ceram. Soc., 1998, 81 (9): 2504--2506. [2] Kitaoka A, Hirota K, Yoshinaka M, et al. J. Am. Ceram. Soc., 2000, 83 (5): 1311--1313. [3] Zhang Y J, Yin Y S, Zhou Y, et al. Interceram, 2000, 49 (1): 36--39. [4] Stoloff N S. Mater. Sci. Eng. , 1998, A258: 1--14. [5] 周玉. 陶瓷材料学. 哈尔滨: 哈尔滨工业大学出版社. 1995. 315--336. [6] 尹衍升. 铁铝金属间化合物. 上海: 上海交通大学出版社. 1996. 20--21. [7] 张长瑞. 陶瓷基复合材料. 长沙: 国防科技大学出版社. 2001. 93--95. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%