使用超音速等离子喷涂设备在45钢基体上制备了Fe基合金涂层,采用扫描电镜、透射电镜等设备对涂层组织结构进行了表征.以球盘式接触疲劳试验机为平台,考察了涂层在1.58、1.84、2.04 GPa 3种应力水平下的接触疲劳寿命.采用Weibull 概率统计方法处理离散的接触疲劳寿命数据,建立了Weibull失效概率统计模型和失效概率-应力-疲劳寿命(P-S-N)曲线图.结果表明,涂层结构致密且呈典型的层状结构,涂层粒子结合界面平整;涂层粒子内部析出弥散分布的点状碳化物,丽在边界处析出连续分布的片状碳化物;涂层微裂纹周围分布有强韧性极高的纳米晶;根据建立的Weibull失效概率统计模型和P-S-N曲线图,可以有效地预测涂层的接触疲劳寿命.
参考文献
| [1] | Stewart S;Ahmed R .Rolling contact fatigue of surface coatings-a review[J].WEAR,2002,253(11-12):1132-1443. |
| [2] | Nieminen R;Vuoristo P;Niemi K .Rolling contact fatigue failure mechanisms in plasma and HVOF sprayed WC-Co coatings[J].WEAR,1997,212(01):66-77. |
| [3] | M. Ciavarella;F. Monno .A comparison of multiaxial fatigue criteria as applied to rolling contact fatigue[J].Tribology International,2010(11):2139-2144. |
| [4] | 徐滨士.再制造工程基础及其应用[M].哈尔滨:哈尔滨工业大学出版社,2005 |
| [5] | 张伟,徐滨士,张纾,梁秀兵,史佩京,刘世参.再制造研究应用现状及发展策略[J].装甲兵工程学院学报,2009(05):1-5,47. |
| [6] | Li X M;Yang Y Y;Shao T M et al.Impact wear performances of Cr3 C2 NiCr coatings by plasma and HVOF spraying[J].WEAR,1997,202(02):208-214. |
| [7] | 陈亚军,王志平,纪朝辉,王立君.等离子与电弧喷涂Ni-Cr-Al涂层结合强度和磨粒磨损性能[J].材料热处理学报,2011(02):119-123. |
| [8] | 赵晓琴,周惠娣,陈建敏.等离子喷涂纳米和常规喂料WC-Co涂层在干摩擦和水环境中的摩擦磨损性能研究[J].摩擦学学报,2006(03):208-213. |
| [9] | Gao Y.;Xu XL.;Yan ZJ.;Xin G. .High hardness alumina coatings prepared by low power plasma spraying[J].Surface & Coatings Technology,2002(2/3):189-193. |
| [10] | S. Zhu;B. Xu;J. Yao .High Quality Ceramic Coatings Sprayed by High Efficiency Hypersonic Plasma Spraying Gun[J].Materials Science Forum,2005(Pt.5):3981-3984. |
| [11] | Y. B. Guo;D. W. Schwach .An experimental investigation of white layer on rolling contact fatigue using acoustic emission technique[J].International Journal of Fatigue,2005(9):1051-1061. |
| [12] | Zhang X C;Xu B S;Wu Y X et al.Porosity,mechanical properties,residual stresses of supersonic plasma-sprayed Ni-based alloy coatings prepared at different powder feed rate[J].Applied Surface Scicence,2008,254(13):3879-3889. |
| [13] | 朴钟宇,徐滨士,王海斗,濮春欢.表征涂层接触疲劳寿命方法的试验研究[J].中国机械工程,2009(13):1616-1618. |
| [14] | 王韶云,李国禄,王海斗,刘金海,徐滨士,朴钟宇.超音速等离子NiCr/Cr_3C_2涂层的接触疲劳寿命[J].材料热处理学报,2012(05):112-115. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%