研究了在烧结混料时运用喷吹轻烧白云石粉工艺,以及不同轻烧白云石粉添加量、水分添加量对烧结混料情况、混料机粘料率和烧结矿冷态强度的影响规律。在此基础上与传统熔剂的添加工艺进行了比较分析并进行了烧结杯试验研究。结果表明：采用喷吹方式加入轻烧白云石粉,与传统配入方式相比,烧结混料情况改善,混合料制粒效果和混匀情况变好,同时粘料率降低0.69%~0.97%,烧结矿的冷态强度略有升高,但变化不大。得出保证烧结矿最佳混料情况和冷态强度的轻烧白云石喷吹量为4.64%,最佳喷吹位置为一混时及w（H2O）=7.5%时。
The effect of addition of light-burned dolomite and water addition amount in mixture of sintering on material sticking condition in sinter mixture and cold strength of sinter was investigated for the process of injection of light-burned dolomite in sintering.The comparative analysis between the new technology and traditional flux addition and sinter pot experiments were carried out.Comparing with traditional application,the results show that after injecting light-burned dolomite powder,the condition of material mixing of sintering is improved,and the pelleting results and uniform mixing of sintering effect become better,meanwhile the rate of material sticking is reduced 0.69%-0.97%,the cold strength of sinter is slightly increased but it changes very little.For the best cold strength,the injection amount is 4.64%.Furthermore,the best injecting position is the primary mixer when water content in mixture is about 7.5%.
参考文献
| [1] | 于素荣,于淑娟,刘艳辉,李跃民.MgO含量对烧结矿烧结指标及冶金性能的影响[J].鞍钢技术,2008(05):23-26. |
| [2] | 姜鑫,吴钢生,魏国,李小钢,沈峰满.MgO对烧结工艺及烧结矿冶金性能的影响[J].钢铁,2006(03):8-11,35. |
| [3] | 高丙寅,张春,邢建民.不同MgO熔剂添加剂的烧结试验及生产[J].河南冶金,2006(03):9-12. |
| [4] | 沈峰满;杜鹤桂;刘新 等.助燃剂对煤粉燃烧等性能的影响[J].东北大学学报(自然科学版),1996,17(02):167. |
| [5] | Eiki K;Yorito S;Takazo K et al.Influence of Properties of Fluxing Materials on the Flow of Melt Formed in the Sinte-ring Process[J].ISIJ International,2000,40(09):857. |
| [6] | 代汝昌.烧结生产用熔剂结构优化的工业试验[J].山东冶金,2004(02):40-42. |
| [7] | 薄涛,王新安,方贻留,韩克峰.烧结矿中MgO配加方式的改进试验[J].山东冶金,2002(01):39-41. |
| [8] | 刘竹林,陈子林,汤乐云.烧结工艺优化的试验研究[J].钢铁,2006(05):15-19. |
| [9] | 武轶,董昀,王富生.烧结矿不同碱度、MgO及SiO2含量水平试验研究[J].山东冶金,2002(06):33-35. |
| [10] | 客海滨,张玉柱,王丽丽,邢宏伟.不同MgO含量对烧结矿质量的影响[J].河南冶金,2007(01):8-10,13. |
| [11] | 赵金龙.MgO对烧结矿性能的影响[J].河北冶金,2008(05):22-25,36. |
| [12] | 于素荣,于淑娟,刘艳辉,李跃民.MgO含量对烧结矿烧结指标及冶金性能的影响[J].鞍钢技术,2008(05):23-26. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%