本文采用两种方法对片状铝粉进行着色,一种方法是采用正硅酸乙酯(TEOS)的溶胶凝胶在铝粉表面包覆一层SiO2的过程中,使颜料共沉积在包覆膜层中,从而使铝粉着色;另一种方法是先将颜料沉积在铝粉表面,再用溶胶凝胶包覆SiO2的方法得到着色铝粉.采用TEM、EDS、及XRD等手段对着色后的铝粉进行分析,考察TEOS用量对包覆情况的影响,并比较两种方法得到的着色铝粉的特点.结果表明:第二种方法着色所需TEOS用量少于第一种方法,两种方法得到的着色铝粉表面均较粗糙.
参考文献
| [1] | Eckart公司 .用于粉末涂料的着色铝粉颜料[J].中国涂料工业,2002,31(01):46-49. |
| [2] | 吴垠,李凤生,白华萍,姜炜,杨毅.金色闪光铝粉颜料的制备研究[J].材料科学与工程学报,2006(06):923-925. |
| [3] | Smith GB.;Gentle A.;Swift P.;Earp A.;Mronga N. .Coloured paints based on coated flakes of metal as the pigment, for enhanced solar reflectance and cooler interiors: description and theory[J].Solar Energy Materials and Solar Cells: An International Journal Devoted to Photovoltaic, Photothermal, and Photochemical Solar Energy Conversion,2003(2):163-177. |
| [4] | Sakka Sumio.Hydrolysis and Polycondensation of Dimethyldiethoxysnane and Methyltriethoxysilane as Materials for the Sol-gel Process[J].Journal of Non-Crystalline Solids,1985(82):24-30. |
| [5] | Wang, D;Bierwagen, GR .Sol-gel coatings on metals for corrosion protection[J].Progress in Organic Coatings,2009(4):327-338. |
| [6] | 林健 .催化剂对正硅酸乙酯水解-聚合机理的影响[J].无机材料学报,1997,12(03):363-369. |
| [7] | 顾宇辉,古宏晨,徐宏,韩哲文.正硅酸乙酯水解过程的半经验量子化学研究[J].无机化学学报,2003(12):1301-1306. |
| [8] | 应皆荣,万春荣,姜长印.用溶胶凝胶法在LiNi0.8Co0.2O2表面包覆SiO2[J].电源技术,2001(06):401-404. |
| [9] | 叶红齐,陈加娜,刘辉,张赢超.片状铝粉表面包覆SiO2薄膜的研究[J].上海涂料,2006(10):15-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%