研究了温度、初始压力、粒度对Ti33V20Cr47合金吸氢动力学性能的影响.研究发现,合金的吸氢过程控速环节为三维扩散,表观活化能为25.7±0.8 kJ/mol.合金的反应速度随温度的升高而加快.由于Ti33V20Cr47合金有2个吸氢平台,在1.5 MPa和2.5 MPa压力下比在3.5 MPa压力下更先完成吸氢.合金反应速度随合金粒度的增大而加快.原因是合金吸氢过程为放热过程,粒度越大,吸氢产生的热量越不容易耗散,温度越高,导致吸氢越快.
参考文献
| [1] | Huang TZ;Wu Z;Xia BJ;Huang TS .Influence of V content on structure and hydrogen desorption performance of TiCrV-based hydrogen storage alloys[J].Materials Chemistry and Physics,2005(2/3):544-547. |
| [2] | Cho S W;Park C N;Yoo J H et al.[J].Journal of Alloys and Compounds,2005,403:262. |
| [3] | Wang J Y;Jeng R R;Nieh J K et al.[J].International Journal of Hydrogen Energy,2007,32:3959. |
| [4] | Song X P;Pei P;Zhang P L et al.[J].Journal of Alloys and Compounds,2008,554:392. |
| [5] | Akiba E;Iba H .[J].Intermetallics,1998,6:461. |
| [6] | Yoo J H;Shim G Choa S W et al.[J].International Journal of Hydrogen Energy,2007,32:2977. |
| [7] | Dou Tao;Wu Zhu;Mao Jianfeng et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2008,476:34. |
| [8] | Yu X B;Wu Z;Li F et al.[J].Applied Physics Letters,2004,84:3199. |
| [9] | Bobet J L;Akiba E;Nakamura Y et al.[J].International Journal of Hydrogen Energy,2000,25:987. |
| [10] | Hu Y Q;Yan C;Zhang H F et al.[J].Journal of Alloys and Compounds,2004,375:265. |
| [11] | Singh B K;Shim G;Cho S W .[J].International Journal of Hydrogen Energy,2007,32:4961. |
| [12] | Pei P;Song X P;Liu J et al.[J].International Journal of Hydrogen Energy,2009,34:8094. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%