Microstructure and phase transformation of Ti46Al8Nb0.5B0.2C alloy have been investigated.X-ray diffraction （XRD）,optical microscopy （OM）,scanning electron microscopy （SEM） and transmission electron microscopy （TEM） results show that as-cast and hot isostatic pressing （HIP） alloy mainly composed of γ and α 2 phase have fully lamellar microstructure with point-like or ribbon-like TiB 2 distributing in lamellar colony or at grain boundary.The mean size of lamellar colony is about 150 and 450 μm for as-cast and HIP alloy,respectively.The lamellar spacing is about 550 and 600 nm for as-cast and HIP alloy,respectively.It has been found that cooling rates and quenching temperatures have significant effect on phase transformation of Ti46Al8Nb0.5B0.2C alloy.When the alloy is treated at 1380℃ for 1 h and cooled from α domain,water cooling leads to complete α → α 2 transformation,oil cooling leads to predominant α → α 2 and part α → γ m transformation,air cooling leads to α → α ＋ γ p2 →L（α ＋ γ） →L（α 2 ＋ γ） transformation,and furnace cooling leads to α → α ＋ γ p3 →L（α ＋ γ） →L（α 2 ＋ γ） transformation.However,when the alloy is treated at 1400℃ for 1 h and cooled from α domain,water cooling leads to predominant α → α 2 and part α → α ＋ γ p4 → γ m transformation,oil cooling leads to α → α ＋ γ p5 → γ m transformation,air cooling leads to α → α ＋ γ p6 →L（α ＋ γ） →L（α 2 ＋ γ） transformation,and furnace cooling leads to α → α ＋ γ p7 →L（α ＋ γ） →L（α 2 ＋ γ） transformation.Microstructural evolution of the alloy during various heat treatments has been examined and the phase transformation mechanisms have been elucidated.Based on the experimental observation,schematic CCT diagrams for the alloy have been given.
参考文献
| [1] | M. Mitoraj;E. Godlewska;O. Heintz .Scale composition and oxidation mechanism of the Ti-46Al-8Nb alloy in air at 700 and 800 °C[J].Intermetallics,2011(1):39-47. |
| [2] | C. Scheu;E. Stergar;M. Schober .High carbon solubility in a gamma-TiAl-based Ti-45Al-5Nb-0.5C alloy and its effect on hardening[J].Acta materialia,2009(5):1504-1511. |
| [3] | H.F. CHLADIL;H. CLEMENS;H. LEITNER .Phase transformations in high niobium and carbon containing gamma -TiAI based alloys[J].Intermetallics,2006(10/11):1194-1198. |
| [4] | W.D.Wang,Y.C.Ma,B.Chen,M.Gao,K.Liu,Y.Y.Li.Effects of Boron Addition on Grain Refinement in TiAl-based Alloys[J].材料科学技术学报（英文版）,2010(07):639-647. |
| [5] | R.M. Imayev;V.M. Imayev;M. Oehring .Alloy design concepts for refined gamma titanium aluminide based alloys[J].Intermetallics,2007(4):451-460. |
| [6] | V. Bauer;H.-J. Christ .Thermomechanical fatigue behaviour of a third generation gamma-TiAl intermetallic alloy[J].Intermetallics,2009(5):370-377. |
| [7] | D. Peter;J. Pfetzing;M.F.-X. Wagner;G. Eggeler.Microstructural anisotropy, uniaxial and biaxial creep behavior ofTi-45A1-5Nb-0.2B-0.2C[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2009:368-372. |
| [8] | U. Kitkamthorn;L.C. Zhang;M. Aindow .The structure of ribbon borides in a Ti-44Al-4Nb-4Zr-lB alloy[J].Intermetallics,2006(7):759-769. |
| [9] | Z.X. LI;C.C. CAO .Effects of minor boron addition on phase transformation and properties of Ti-47.5Al-2Cr-2Nb alloy[J].Intermetallics,2005(3/4):251-256. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%