以电石渣和白碳黑分别作为钙质和硅质原料,采用水热法制备具有磷回收特性的水化硅酸钙。研究了制备条件对水化硅酸钙磷回收性能的影响,采用XRD揭示了水化硅酸钙的磷回收机制。通过BET、SEM表征了水化硅酸钙的微观结构,考察了水化硅酸钙的溶钙供碱能力。钙硅摩尔比为1.6∶1,水热反应温度为170℃,水热反应时间为4.5h,搅拌强度为90r/min的条件下所制备的水化硅酸钙,其磷回收产品中的磷含量达到18.64%。该材料具有多孔结构,比表面积达到113.3572m2/g,能够溶出的Ca2＋浓度为3.52mg/g,这些溶钙供碱特性使得该材料能够在pH值=9.0的环境下以羟基磷酸钙的形式从污水中回收磷。
Calcium silicate hydrate with phosphorus recovery efficiency was synthesized by carbide residue and silica. Effect of prepared method on phosphorus recovery efficiency of calcium silicate hydrate was studied. Mechanism of phosphorus recovery was revealed by XRD. Microstructure of calcium silicate hydrate was characterized by BET and SEM. Capacity of Ca^2+ and OH release was investigated. The considerable preparation conditions are obtained on the condition of Ca/Si molar ratio 1.6 - 1, reaction temperature 170℃, reaction time 4.5h, stirring intensity 90r/min. Phosphorus content of product of phosphorus recovery reached 18.64. The prepared calcium silicate hydrate has a high BET surface area 113. 3572m^2/g with porous structure. Concentration of Ca^2+ release reached 3.52mg/g. This material could recover phosphorus from wastewater in the form of hydroxyl calcium phosphate on the condition of pH=9.
参考文献
| [1] | Maoqiang Li,Hongxun Liang.FORMATION OF MICRO-POROUS SPHERICAL PARTICLES OF CALCIUM SILICATE (XONOTLITE) IN DYNAMIC HYDROTHERMAL PROCESS[J].中国颗粒学报（英文版）,2004(03):124-127. |
| [2] | Alexandra A.P. Mansur;Herman S. Mansur .Preparation, characterization and cytocompatibility of bioactive coatings on porous calcium-silicate-hydrate scaffolds[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2010(2):288-294. |
| [3] | 廖其龙,徐光亮,尹光福,周大利,郑昌琼,李晓东.纳米羟基磷灰石的水热合成[J].功能材料,2002(03):338-340. |
| [4] | Battistoni P.;Pavan P.;Prisciandaro M.;Cecchi F.;De Angelis A. .Phosphorus removal from a real anaerobic supernatant by struvite crystallization[J].Water research: A journal of the international water association,2001(9):2167-2178. |
| [5] | Berg U;Donnert D;Weidler PG;Kaschka E;Knoll G;Nueesch R .Phosphorus removal and recovery from wastewater by tobermorite-seeded crystallisation of calcium phosphate[J].Water Science and Technology,2006(3):131-138. |
| [6] | Berg U;Donnert D;Ehbrecht A;Bumiller W;Kusche I;Weidler PG;Nuesch R ."Active filtration" for the elimination and recovery of phosphorus from waste water[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2005(1/3):141-148. |
| [7] | Sinirkaya M;Kadir Ozer A;Sahin Gulaboglu M .Investigation of the changes of P2O5 content of phosphate rock during simultaneous ealcination/sulfation[J].Powder Technology,2011,211:72-76. |
| [8] | Jeffrey J. Chen;Jeffrey J.Thomas;Hal F.W.Taylor .Solubility and structure of calcium silicate hydrate[J].Cement and Concrete Research,2004(9):1499-1519. |
| [9] | P. BATTISTONI;P.PAVAN;M. PRlSCIANDARO .STRUVITE CRYSTALLIZATION: A FEASIBLE AND RELIABLE WAY TO FIX PHOSPHORUS IN ANAEROBIC SUPERNATANTS[J].Water research: A journal of the international water association,2000(11):3033-3041. |
| [10] | Sukalyan Sengupta;Arka Pandit .Selective removal of phosphorus from wastewater combined with its recovery as a solid-phase fertilizer[J].Water research: A journal of the international water association,2011(11):3318-3330. |
| [11] | 闵智,甘民,左宁,吉芳英.SBR侧流除磷工艺低成本化学除磷及磷回收潜能分析[J].宁夏大学学报（自然科学版）,2011(02):154-158. |
| [12] | I.G. Richardson .The calcium silicate hydrates[J].Cement and Concrete Research,2008(2):137-158. |
| [13] | E. Bonaccorsi;S. Merlino;H.F.W.Taylor .The crystal structure of jennite, Ca_9Si_6O_(18)(OH)_6-8H_2O[J].Cement and Concrete Research,2004(9):1481-1488. |
| [14] | Alexandra A.P. Mansur;Herman S. Mansur .Preparation, characterization and cytocompatibility of bioactive coatings on porous calcium-silicate-hydrate scaffolds[J].Materials science & engineering, C. Biomimetic and supramolecular systems,2010(2):288-294. |
| [15] | Daisuke S;Tomonari F .A thermodynamic model of dissolution and precipitation of calcium silicate hydrates[J].Cement and Concrete Research,2006,36:227-237. |
| [16] | 张文生,叶家元,王妍萍,王宏霞,王渊,李永鑫.掺杂有机大分子水化硅酸钙的孔结构及表面分形特征[J].硅酸盐学报,2006(12):1497-1502. |
| [17] | Yun Liu;Xia Sheng;Yuanhua Dong.Removal of high-concentration phosphate by calcite: Effect of sulfate and pH[J].Desalination: The International Journal on the Science and Technology of Desalting and Water Purification,2012:66-71. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%