Water blown rigid polyurethane foams with different functionality were prepared.The physical properties of rigid foams were measured with rotational viscometer(NDJ-1),universal testing machine(lnstron3365),scanning electron microscope(SEM)and differential scanning calorimeter(DSC).The results show that the viscosity of polyether polyol increases exponentially from 62 mPa s to 6 000 mPa s with theincrease of functionality from 2 to 5.6,respectively.The overall density of foam increases slightly from 31.7kg/m3 to 37.4 kg/m3 with increasing functionality while core density exhibited little difference.Compressive strength of foam shows the similar behavior with density except for 2-functional sample.At the same time,dimensional stability becomes better with increasing functionality except for 5.6-functional foam that has worse stability than 4.8-functional foam.From the SEM results,the functionality is not an important factor in determining distribution of cell size of foam.According to the results of thermal analysis,the glass transition temperature(T)shifts to a higher temperature from 128.9℃ to 166.3℃ for the 2 to 5.6 functional foam,respectively.

参考文献

[1] C G Potts;L M Draaijer .Development s in Rigid Polyurethane Foams for the Insulation of District Heating Pipelines[J].Journal of Cellular Plastics,1985,21(01):51-57.
[2] Demharter A. .Polyurethane rigid foam, a proven thermal insulating material for applications between +130(degrees)C and -196(degrees)C[J].Cryogenics,1998(1):113-117.
[3] M J Molina;F S Rowland .Stratospheric Sink for Chlorofluoromethanes:Chlorine Atomic-catalysed Destruction of Ozone[J].Nature,1974,249(5460):810-812.
[4] H J M Grunbauer;J C Folmer;H C Vanlieshout et al.The Effect of Polyol Miscibility on Polymer Morphology of Water Blown Rigid Polyurethane Insulation Foam[J].Polymeric Preprints(American Chemical Society Division of Polymer Chemistry),1991,32(01):517-518.
[5] W Rainer;Leverkusen;Colonge et al.Substantially Closed Cell Rigid Foams Containing Urethane,Urea and Biuret Groups and a Process for Their Production[P].US 5070115,1991-12-03.
[6] W Donald;Schumacher;M George et al.Process for Production of Low Density Water Blown Rigid Foams with Flow and Dimensional[P].US 5627221,1997-05-06.
[7] R Tabor;J Lepovitz;W Potts et al.The Effect of Polyol Functionality on Water Blown Rigid Foams[J].Journal of Cellular Plastics,1997,33(04):372-399.
[8] 李小斌,曹宏斌,张懿.全水发泡硬质聚氨酯泡沫塑料技术研究进展[J].中国塑料,2004(07):1-4.
[9] Seo WJ.;Jung HC.;Hyun JC.;Kim WN.;Lee YB.;Choe KH.;Kim SB. .Mechanical, morphological, and thermal properties of rigid polyurethane foams blown by distilled water[J].Journal of Applied Polymer Science,2003(1):12-21.
[10] H.C.Jung;S.C.Ryu;W.N.Kim;Y.-B.Lee;K.H.Choe;S.-B.Kim .Properties of Rigid Polyrethane Foams Blown by HCFC 141B and Distilled Water[J].Journal of Applied Polymer Science,2001(2):486-493.
[11] J B Nichols;D Bhattacharjee;O Moreno et al.Reduced Density Carbon Dioxide Blown Foam Based on Novel Polyol Technology[J].Journal of Cellular Plastics,1996,32(02):139-153.
[12] Goods SH.;Henderson CC.;Skala DM.;Neuschwanger CL. .Mechanical properties of CRETE, a polyurethane foam[J].Journal of Applied Polymer Science,1998(7):1045-1055.
[13] C Cecchini;R Zannetti;A Stefani .Dimensional Stability of Polyurethane Rigid Foams Blown with CO2[J].Journal of Cellular Plastics,1999,35(06):514-530.
[14] D L Christaman;C J Reichel .Water-blown Rigid Foams[J].Journal of Cellular Plastics,1996,32(01):82-96.
[15] H J M Grunbauer;J A Thoen;J C W Folmer et al.Polymer Morphology of Water-blown Rigid Polyurethane Foams:Development of New Polyols[J].Journal of Cellular Plastics,1992,28(01):36-47.
[16] T Kaiser .Highly Crosslinked Polymers[J].Progress in Polymer Science,1989,14(03):373-450.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%