以含硼季铵盐（N-甲基溴代十二烷基二乙醇胺硼酸酯）作为新型焦炭劣化抑制剂,考察其对焦炭的热态性能改善影响,并对焦炭结构和形貌进行表征,初步探讨了含硼季铵盐改善焦炭热态性能的机理。结果表明：喷洒含硼季铵盐溶液后焦炭热态性能指标得到明显改善,1.0%的含硼季铵盐能使焦炭反应性CRI降低8.69%,反应后强度CSR提高7.94%,焦炭表面积、气孔直径和深度显著减小,减弱了二氧化碳对焦炭的侵蚀劣化作用,这为改善焦炭性能指标开拓了新途径。
The effect of spraying boron quaternary ammonium salt（which was as a new type deterioration inhibitor） on coke thermal property was investigated.The structure and morphology of coke were scanned for explaining boron quaternary ammonium salt＇s inhibition mechanism to coke by SEM.The results indicate that the coke reactivity index（CRI） is decreased by 8.69% and the coke strength after reaction（CSR） is improved by 7.94% when spraying 1.0% boron quaternary ammonium salt on coke samples.The SEM scanning results show that the coke surface pore diameter and the depth decrease,this helps to reduce CO2 to erode coke.
参考文献
| [1] | 周师庸;赵俊国.炼焦煤性质与高炉焦炭质量[M].北京:冶金工业出版社,2005 |
| [2] | 张泽志,王留成,王福安.抑制焦炭劣化技术研究进展[J].化学世界,2010(07):438-442. |
| [3] | 刘德军,王尤清,于淑娟,张立国,安云沛.提高焦炭热态性能的钝化处理技术研究[J].中国冶金,2006(12):27-30. |
| [4] | 张泽志,王建设,宋成盈,赵建宏,王留成,王福安.淀粉改善焦炭热态性能及其机理研究[J].煤炭转化,2010(04):40-42. |
| [5] | Kushnarev A V;Kirichkov A A;Berkutov N A et al.Optimizing the Coking Coal Employed at OAO NTMK to Ensure Competitive CSR and CRI Values of Coke[J].Steel In Translation,2007,37(11):948. |
| [6] | 刘昔跃,徐君,张雅茹,崔文亮.焦炭的钝化处理研究[J].煤炭转化,2008(02):44-47. |
| [7] | 王留成,郑士朋,王建设,宋成盈,赵建宏.焦炭劣化抑制剂对焦炭热性能的改善研究[J].钢铁,2009(05):16-18. |
| [8] | 杨雪峰,朱子宗,张竹明,唐启荣,张昆华,赵先胜,高芸祥,李轶.焦炭喷洒ZBS添加剂在高炉上的应用[J].钢铁研究学报,2006(02):59-62. |
| [9] | 龙晓阳,潘彤.吸附法改善焦炭热性质的研究[J].鞍钢技术,2005(02):15-19. |
| [10] | 吴信慈,杨俊和,张群,何深奇,张琢.CH4化学气相渗透沉积提高焦炭热性质研究[J].钢铁,2005(04):12-16. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%