套管在静水压试验时发生爆裂的原因

机械工程材料, 2012, 36(3): 97-100.

套管在静水压试验时发生爆裂的原因

张春婉 ^1, , 张国正 ^2, , 史李镛 ^3, , 张凤娟 ^4,

1.西安摩尔石油工程实验室,西安710065

2.西安摩尔石油工程实验室,西安710065

3.山西北方风雷工业集团有限公司,太原030009

4.西安应用光学研究所,西安710065

关键词：静水压试验 , 爆裂 , 淬火裂纹 , 套管

Cracking Reason of Casings during Hydrostatic Test

Keywords： hydrostatic test , cracking , quenching crack , casing

通过宏观形貌和显微组织观察、化学成分分析和断口分析等方法,对两根套管在静水压试验过程中发生爆裂的原因进行了分析。结果表明：套管发生纵向爆裂的原因是热处理工艺参数选择不合理,导致管体内表面存在淬火裂纹,致使套管在静水压试验中因不能承受压力过载而发生爆裂。

The cracking reason of two casings during hydrostatic test was analyzed by means of macrograph and microstructure observation,chemical composition analysist and fracture analysis,et al.The results show that the reason of the casings longitudinal cracking was improper heat treatment process parameters,which resulted in the quenching cracks appeared on the inner surface of casings,and the quenching cracks led to the casings could not endure pressure overload during hydrostatic test.

参考文献

[1]	成海涛.我国无缝钢管行业的现状分析[J].钢管,2006(03):1-6.
[2]	彭在美."十一五"期间中国钢管市场需求预测[J].焊管,2007(05):12-18.

上一张下一张

计量

下载量()
访问量()

作者相关

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网