对代替铬酸盐溶液的镀锌钛盐钝化技术进行了研究,并借助扫描电镜、电子能谱仪考察了钝化工艺对钝化膜色泽的影响情况.结果表明,在钛盐钝化液中,镀锌层表面可获得黄、蓝、金黄、紫、绿等色泽的钝化膜;钝化工艺参数(钝化时间、钝化温度、钝化液pH值、干澡温度等)对镀锌层钝化膜的色泽有很大影响;镀锌钛盐钝化膜的微观形貌、表面成分与不同钝化工艺条件下获得的钝化色泽具有一定的对应关系.初步探讨了镀锌层在钛盐钝化液中成膜产生色泽的原因.
参考文献
| [1] | 张允诚;胡如南;向荣.电镀手册[M].北京:国防工业出版社,1997:256-257. |
| [2] | Tang P T;Bech-Nielsen G;Moiler P M .Molybdate Based Alternatives to Chromating as Passivation Treatment for Zinc[J].Plating and Surface Finishing,1994,81(11):20. |
| [3] | Tang P T;Bech-Nielsen G;Moiler P M .Molybdate Based Passivation of Zinc[J].Tram IMF,1997,75(04):144. |
| [4] | 刘小虹,颜肖慈.镀锌层钼酸盐转化膜及其耐蚀机理[J].电镀与环保,2002(06):17-19. |
| [5] | Hinton B R W;Wilson L .The Corrosion Inhibition of Zinc with Cerous Chloric[J].Corrosion Science,1989,29(09):967. |
| [6] | Montemor M F;Sim~es A M;Ferreira M G S .Composition and behaviour of cerium films on galvanized steel[J].Progress in Organic Coatings,2001,43:274-281. |
| [7] | 龙晋明,韩夏云,杨宁,郭忠诚.锌和镀锌钢的稀土表面改性[J].稀土,2003(05):52-56. |
| [8] | 王济奎;方景礼 .镀锌层表面混合稀土钝化膜的研究[J].中国稀土学报,1997,15(01):31-34. |
| [9] | 李鸿宾,陈建设,刘辉,魏绪钧.热镀锌表面铈盐钝化[J].材料与冶金学报,2002(03):203-205. |
| [10] | 张洪生 .无毒植酸在金属防护中的应用[J].电镀与涂饰,1999,18(04):38-40. |
| [11] | 朱传方;胡腊生.植酸在镀锌钝化中的应用[J].精细化工,1995(12):54-55. |
| [12] | 胡会利,李宁,程瑾宁.镀锌植酸钝化膜耐蚀性的研究[J].电镀与环保,2005(06):21-25. |
| [13] | 杨飞;朱立群 .环保型镀Zn蓝白色钝化及钛盐蓝白钝化的研究与进展[J].表面科学与工程,2006,3(01):34-38. |
| [14] | 朱立群,杨飞.环保型镀锌层蓝色钝化膜耐腐蚀性能的研究[J].腐蚀与防护,2006(10):503-507. |
| [15] | 朱立群,杨飞,黄慧洁,丁楠.镀锌层无铬钛盐的蓝色钝化[J].江苏大学学报（自然科学版）,2007(02):127-130. |
| [16] | 卢燕平,屈祖玉,卢琳,任玉苓.钛（Ⅳ）离子改性低铬钝化膜的研究[J].表面技术,2001(05):39-42. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%