选取Co、Zn、Ca、Mg、Cu和Mn元素与Ni元素以一定化学计量比共沉积,并对其进行修饰或掺杂,制备出新型氢氧化镍正极材料.采用恒电流充放电技术测试其在不同温度不同倍率下的充放电性能,并测试了样品的粒径和振实密度.研究结果表明:粒径尺寸分布适中,振实密度较高;通过多元素协同掺杂,可显著提高析氧电位,抑制析氧副反应的发生.多元素之间的协同掺杂是改善氢氧化镍正极材料高温大电流充放电性能的有效途径.
参考文献
| [1] | 宋全生,唐致远,郭鹤桐.钴的添加对涂膏型镍电极电化学性能的影响[J].电源技术,2004(05):282-284,299. |
| [2] | X. -Y. Wang;J. Yan;Z. Zhou .Electrochemical characteristics of nickel hydroxide modified by electroless cobalt coating[J].International journal of hydrogen energy,1998(10):873-878. |
| [3] | Ying T .Surface modification of nickel hydroxide particles by micro-sized cobalt oxide hydroxide and properties as electrode materials[J].Surface & Coatings Technology,2005(7):2376-2379. |
| [4] | Fierro C;Fetcenko M A .Nickel Hydroxide Positive Electrode Material Exhibiting Improved Conductivity and Engineered Activation Energy[P].EP:1672724A2,2006-06. |
| [5] | Fetcenko M A.Evolution.Current Status and Future of NiMH Battery Technology[A].,2006 |
| [6] | C. Fierro;A. Zallen;J. Koch .The Influence of Nickel-Hydroxide Composition and Microstructure on the High-Temperature Performance of Nickel Metal Hydride Batteries[J].Journal of the Electrochemical Society,2006(3):A492-A496. |
| [7] | Fetcenko M A;Ovshinsky S R;Reichman B et al.Recent Advances in NiMH Battery Technology[J].Journal of Power Sources,2007,165:544-551. |
| [8] | He X M;Ren J G;Li W et al.Ca3(PO4)2 Coating of Spherical Ni(OH)2 Cathode Materials for Ni-MH Batteries at Elevated Temperature[J].Electrochimica Acta,2006,51:4533-4536. |
| [9] | 危亚辉;贺万宁;沈湘黔 等.球形氢氧化镍表面修饰方法[P].CN1560940A,2005-01-05. |
| [10] | Li W;He XM;Ren JG;Jiang CY;Wan CR .Oxygen evolution improvement of Ni(OH)(2) by Ca-3(PO4)(2) coating at elevated temperature[J].Journal of Electroanalytical Chemistry: An International Journal Devoted to All Aspects of Electrode Kinetics, Interfacial Structure, Properties of Electrolytes, Colloid and Biological Electrochemistry,2006(2):127-129. |
| [11] | 李稳 .球形氢氧化镍高温性能的研究[D].北京:清华大学,2005. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%