研究了轧辊用高碳高钒高速钢的微观组织结构及添加不同变质剂处理后对其组织和性能的影响.结果表明:该高速钢的组织为马氏体、奥氏体及MC和M2C型碳化物.添加0.3 %的稀土变质时,组织中碳化物分布状况的改善不明显,但可以促进加热过程中网状碳化物的断网和球团化;添加0.1 %的镁变质时,组织中共晶碳化物明显减少,碳化物网得到细化;添加1.0 %的钛或添加RE-Ti-Mg复合变质剂对碳化物的类型转变影响不大,但可以明显细化晶粒和共晶碳化物网.添加RE-Ti-Mg复合变质剂处理后组织中的共晶碳化物网基本上得到消除.
参考文献
| [1] | 邵素云;王刚;宋威.谈高速钢轧辊[J].轧钢,1996(02):37-40. |
| [2] | 刘海峰,刘耀辉.高速钢复合轧辊的研究现状及进展[J].钢铁研究学报,1999(05):67-71. |
| [3] | Sano Y;Hattori T;Haga M .Characteristics of High Carbon HighSpeed Steel Rolls for Hot Strip Mill[J].ISIJ International,1992,32(11):1194-1201. |
| [4] | HashimotoM;Otomo S;Yoshida K et al.Development of High-Performance Roll by Continuous Pouring Process for Cladding[J].ISIJ International,1992,32(11):1202-1210. |
| [5] | Keun C H;Sunghak L;Hui C L .Effects of Alloying Elements onMicrostructure and Fracture Properties of Cast High Speed SteelRolls[J].Materials Science and Engineering,1998,254(01):282-295. |
| [6] | Joon W P;Hui C L;Sunghak L .Composition,Microstructure,Hardness and Wear Properties of High Speed Steel Rolls[J].Metallurgical and Materials Transactions,1999,30:399-408. |
| [7] | 罗迪;邢国华;邹惠良 等.S,P在高速钢晶界上的偏聚和稀土元素的净化作用[J].金属学报,1983,19(04):151-156. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%