采用静电纺丝法,以丝素(SF)、胶原(COL)混合聚左旋乳酸(PLLA)和聚(左旋乳酸-己内酯)(PLCL),制备不同质量配比的SF/COL/PLLA和SF/COL/PLCL三维纳米纤维支架材料,采用傅里叶红外光谱(FTIR)分析高分子聚合物对丝素、胶原结构的影响,测量接触角以检测其亲水性能.结果表明:高分子聚合物破坏丝素胶原之间形成的氢键,使以β折叠结构为主的SF变为以无规卷曲和α螺旋结构为主;当SF/COL与高聚物质量比为70∶30时,接触角θ<90°,液体对三维纳米纤维支架材料的润湿性较好,且SF/COL/PLCL的亲水性比SF/COL/PLLA的亲水性更优.
参考文献
[1] | 夏永林 .湿法纺PEG/PLA和静电纺SF/PLA的研究[D].苏州大学,2007. |
[2] | Xiao W;He J;Nichol JW;Wang L;Hutson CB;Wang B;Du Y;Fan H;Khademhosseini A .Synthesis and characterization of photocrosslinkable gelatin and silk fibroin interpenetrating polymer network hydrogels.[J].Acta biomaterialia,2011(6):2384-2393. |
[3] | Oliveira,A.L.;Sun,L.;Kim,H.J.;Hu,X.;Rice,W.;Kluge,J.;Reis,R.L.;Kaplan,D.L. .Aligned silk-based 3-D architectures for contact guidance in tissue engineering[J].Acta biomaterialia,2012(4):1530-1542. |
[4] | Santin M;Motta A;Freddi G et al.In vitro evaluation of the inflammatory potential of the silk fibroin[J].Journal of Biomedical Materials Research,1999,46(03):382. |
[5] | Horan RL;Antle K;Collette AL;Wang Y;Huang J;Moreau JE;Volloch V;Kaplan DL;Altman GH .In vitro degradation of silk fibroin.[J].Biomaterials,2005(17):3385-3393. |
[6] | 边瑞琦 .再生丝素蛋白/左旋聚乳酸——聚己内酯共聚物复合纳米纤维膜支架的制备及性能研究[D].浙江理工大学,2012. |
[7] | Min B M;Young Y;Kim J M et al.Formation of nanostructured poly(lactic-co-glycolic acid)/chitin matrix and its cellular response to normal human kenatinoccytes and fibroblasts[J].Carbohydrate Polymers,2004,57(03):285. |
[8] | Wan-Ju Li;Cato T. Laurencin;Edward J. Caterson .Electrospun nanofibrous structure: A novel scaffold for tissue engineering[J].Journal of biomedical materials research, Part B. Applied biomaterials,2002(4):613-621. |
[9] | Lin, H.-Y.;Kuo, Y.-J.;Chang, S.-H.;Ni, T.-S. .Characterization of electrospun nanofiber matrices made of collagen blends as potential skin substitutes[J].Biomedical materials,2013(2):025009-1-025009-9. |
[10] | 张慧,程爱琳.电纺纳米纤维构建组织工程支架研究新进展[J].材料导报,2009(09):88-93. |
[11] | Sun, X.;Wu, L. .Synthesis and properties of crystalline dicarboxylated poly(L-lactic acid) prepolymers[J].Journal of Applied Polymer Science,2011(6):3246-3251. |
[12] | Matthew C Phipps;William C Clem;Shane A Catledge et al.Mesenchymal stem cell responses to bone-mimetic electrospun matrices composed of polycaprolactone,collagen Ⅰ and nanoparticulate hydroxyapatite[J].PLoS One,2011,6(02):e16813. |
[13] | 崔新爱 .静电纺胶原/丝素复合微纳米纤维支架的制备及性能研究[D].天津医科大学,2012. |
[14] | Agarwal M;Koelling K W;Chalmers J J .Characterization of the degradation of polylactic acid polymer in a solid substrate environment[J].Biotechnology Progress,1998,14(03):517. |
[15] | Lalla J K;Chugh N N .Efeets of morphology,conformation and configuration on the IR and raman spectra of various poly(lactic acid)[J].Indian Drugs,1990,27(10):516. |
[16] | Park J W;Lee D J;Yoo E .Melttheology of poly(lactic acid):Consequenees of blending chain architeettires[J].KOREA POLYMER JOURNAL,1999,7(02):93. |
[17] | Elzubair A;Elias CN;Suarez JC;Lopes HP;Vieira MV .The physical characterization of a thermoplastic polymer for endodontic obturation.[J].Journal of dentistry,2006(10):784-789. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%