采用单电子转移-活性自由基聚合(SET-LRP)法合成了活性聚丙烯酸丁酯(L-PBA),采用核磁共振谱仪对其分子结构进行了表征;通过改变单体/引发剂摩尔比,二次引发的单体/大分子引发剂摩尔比,以及多级引发3种途径验证了L-PBA具有反应活性,并且发现L-PBA的相对分子质量可以进行控制;当采用L-PBA再次引发BA聚合时,可在较短时间内(3.5h)、单体/大分子引发剂摩尔比较高时(6665/1),获得较高单体转化率(31.3%),表明大分子引发剂比小分子引发剂活性高;凝胶渗透色谱结果还显示,多级引发所得L-PBA的相对分子质量分布,随单体/大分子引发剂摩尔比及引发级数的增加而变宽,当产物相对分子质量达到19万左右时产物相对分子质量分布出现双峰,原因与体系中活性种与休眠种间快速转换的失衡有关.

参考文献

[1] Pakula, T.;Koynov, K.;Boerner, H.;Huang, J.;Lee, H.-I.;Pietrasik, J.;Sumerlin, B.;Matyjaszewski, K. .Effect of chain topology on the self-organization and the mechanical properties of poly(n-butyl acrylate)-b-polystyrene block copolymers[J].Polymer: The International Journal for the Science and Technology of Polymers,2011(12):2576-2583.
[2] You, B.;Zhou, D.;Yang, F.;Ren, X. .Synthesis and characterization of core-shell polyacrylate particles containing hindered amine light stabilizers[J].Colloids and Surfaces, A. Physicochemical and Engineering Aspects,2011(1):365-370.
[3] 武佳韦,潘明旺,袁金凤,刘通,张留成.SBA/PVC复合树脂的制备与表征[J].高分子学报,2009(07):613-619.
[4] 袁立焕,袁金凤,潘明旺,姚小丽,张留成.PVC基热塑性弹性体的制备与性能[J].高分子材料科学与工程,2010(08):124-127.
[5] Shims Tolue;Mohammad Reza Moghbeli;Seyed Mehdi Ghafelebashi .Preparation of ASA (acrylonitrile-styrene-acrylate) structural latexes via seeded emulsion polymerization[J].European Polymer Journal,2009(3):714-720.
[6] Coelho JFJ;Silva AMFP;Popov AV;Percec V;Abreu MV;Goncalves PMOF;Gil MH .Single electron transfer-degenerative chain transfer living radical polymerization of N-butyl acrylate catalyzed by Na2S2O4 in water media[J].Journal of Polymer Science, Part A. Polymer Chemistry,2006(9):2809-2825.
[7] Percec V;Ramirez-Castillo E;Popov AV;Hinojosa-Falcon LA;Guliashvili T .Ultrafast single-electron-transfer/degenerative-chain-transfer mediated living radical polymerization of acrylates initiated with iodoform in water at room temperature and catalyzed by sodium dithionite[J].Journal of Polymer Science, Part A. Polymer Chemistry,2005(10):2178-2184.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%