采用涂盐方法研究了不同Cr含量镍基高温合金的热腐蚀过程,利用XRD确定腐蚀产物相结构和采用电子探针观察腐蚀层前沿元素分布情况.结果表明,在900℃涂盐条件下,随着Cr含量增加,合金的热腐蚀抗力逐渐增强.合金中加入Cr后,能促使合金表层形成致密、连续的Cr2O3层,并且随着Cr含量增加,Cr2O3层厚度增加,Al2O3层逐渐向外腐蚀层迁移,从而提高了合金的热腐蚀抗力.
参考文献
| [1] | Starr F;Wood N;Roberts R .Investigation of hot salt corrosion at a land-based gas turbine installation[J].Journal de Physique Ⅳ,1993,3(09):779-786. |
| [2] | Otsuka N;Rapp R A .Effect of chromate and vanadate anions on the hot corrosion of preoxidized Ni by a thin fused Na2 SO4 film at 900℃[J].Journal of the Electrochemical Society,1990,137(01):53-60. |
| [3] | Sidhu TS;Agrawal RD;Prakash S .Hot corrosion of some superalloys and role of high-velocity oxy-fuel spray coatings - a review[J].Surface & Coatings Technology,2005(1/3):441-446. |
| [4] | 管秀荣,关英双,纪慧思,刘恩泽,郑志,于永泗.Ru含量对镍基高温合金抗热腐蚀性能的影响[J].材料热处理学报,2013(08):68-73. |
| [5] | 阳志安;肖耀天;师昌绪 .Co对镍基高温合金热强性能影响的研究[J].金属学报,1983,19(04):300-308. |
| [6] | 管秀荣,魏健,刘恩泽,郑志,佟健.Ti含量对镍基高温合金抗热腐蚀性能的影响[J].稀有金属材料与工程,2012(11):1990-1994. |
| [7] | Wu W T;Rahmel A;Schorr M .Role of platinum in the Na2SO4-induced hot corrosion resistance of aluminum diffusion coatings[J].Oxidation of Metals,1984,22(1-2):59-81. |
| [8] | Wu W T;Rahmel A .Acid and basic fluxing of Ni-base superalloys in a 90Na2 SO4-10K2SO4 melt at 1173k[J].Oxidation of Metals,1983,19(5-6):201-229. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%