研究了T122铁素体型耐热钢中铜含量0~1.77%变化对组织与性能影响,结果表明铜含量增加,使钢中8铁素体含量下降,钢的室温和高温强度明显提高.持久强度和长时时效后高温强度也随铜含量增加,明显提高.含铜0.90%时,钢的强度和塑性匹配最佳.
The effect of copper content varying from 0%to 1.77%on the microstructure and properties of T122 heat resistant steel was investigated.The results show that the increase of copper content in the steel leads to the decrease of δ-ferrite amount.The strength at room temperature and high temperature increase obviously.Creep rupture strength and high temperature strength after aging are improved evidently with the increase of copper con-tent,and steel with copper 0.90%content have the optimal matching between strength and plasticity.
参考文献
[1] | Sawaragi Y;Iseda A;Ogawa K;D.Coutsouradis.Materials for Advanced Power Engineering[M].Dordrecht,the Netherlands:Kluwer Academic Publishers,1994 |
[2] | Sawaragi Y;Miyata K.Advanced Heat Resistant Steel for Power Generation[M].San Sebastian,Spain,1998 |
[3] | Fujimitsu MASUYAMA .History of Power Plants and Progress in Heat Resistant Steels[J].ISIJ International,2001(6):612-625. |
[4] | 孙珍宝.铜在钢中的作用[A].北京:冶金工业出版社,1984:9. |
[5] | Superheater,and Heat-Exchanger Tubesl,A 213/A 213M-04b.Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler[S].,2004. |
[6] | 包汉生 .钒对T122铁索体型耐热钢组织与性能的影响[D].秦皇岛:燕山大学,2005. |
[7] | Kadoya Y;Magoshi R.Development of High and Low Pressure Rotor Forgings for High Temperature Steam Turbine[A].Balatonfüred,1997:10. |
[8] | Kimura K;Sawada K.Degradation Behaviour and LongTerm Creep Strength of 12Cr Ferritic Creep Resistant Steels[A].Liege,Belgium,2006 |
[9] | Mats Hāttestrand;Martin Schwind;Hans-Olof Andrén.Microanalysis of Two Creep Resistant 9-12% Chromium Steels[J].Materials Science and Engineering A,1998(250):27. |
[10] | Yuichi FUTAMURA;Toshihiro TSUCHIYAMA;Setsuo TAKAKI .Strengthening Mechanism of Cu bearing Heat Resistant Martensitic Steels[J].ISIJ International,2001(Suppl.):106-110. |
[11] | 杨岩,程世长,杨钢.铜含量对Super304H钢持久性能的影响[J].机械工程材料,2002(10):23-25. |
[12] | Habibi H R .Atomic Structure of the Cu Precipitates in Two Stages Hardening in Maraging Steel[J].Materials Letters,2005,59:1824. |
[13] | 杨岩 .铜含量对Super304H钢性能影响的研究[D].钢铁研究总院,2001. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%