将高能球磨后的Ti-Al粉末和TiC,Al2O3粉末混合进行热压烧结,在烧结的过程中反应生成金属间化合物为增强相的复合材料.通过对粉料的X射线衍射分析、热分析(DSC)和烧结体的成分分析表明,最终的金属间化合物只有Ti3Al而没有其它金属间化合物相.通过热力学计算,分析了反应烧结过程并发现在低温由固相间原子扩散控制生成TiAl3,TiAl,Ti3Al的渐进过程,和在高温下金属间化合物的合成机理,而且增强相和基体界面间处于稳定状态.
参考文献
| [1] | Durlm N .[J].Journal of the European Ceramic Society,1999,19:2415. |
| [2] | Sun-Yong Ahn;Seong-Won Kim;Shinhoo Kang .Microstructure of Ti(CN)-WC-NbC-Ni Cermets[J].Journal of the American Ceramic Society,2001(4):843-849. |
| [3] | 宋桂明,武英.碳纤维增强TiC复合材料的制备与高温强度[J].材料工程,2001(09):3-6,17. |
| [4] | Chou W B;Tuan W H;Chang S T .[J].British Ceramic Transactions,1996,95(02):71. |
| [5] | Sglavo V M;Marino F;Zhang B R .[J].Materials Science and Engineering,1997,239-240:665. |
| [6] | Kevin P. Plucknett;Paul F. Becher .Processing and Microstructure Development of Titanium Carbide-Nickel Aluminide Composites Prepared by Melt Infiltration/Sintering (MIS)[J].Journal of the American Ceramic Society,2001(1):55-61. |
| [7] | Subramanian R;Schneibel J H .[J].Materials Science and Engineering,1997,239-240:633. |
| [8] | 齐民;朱敏;杨大智 .[J].材料科学与工程,1994,12(03):61. |
| [9] | 李小强,胡连喜,王尔德.Ti-Al二元粉末机械合金化过程中组织结构的变化[J].稀有金属材料与工程,2001(03):183-186. |
| [10] | 张俊红,黄伯云,贺跃辉,鲁世强.Ti-46at%Al机械合金化过程中的显微组织演变[J].稀有金属材料与工程,2002(06):440-444. |
| [11] | Davis R M;Mcdermott B;Koch C C .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1988,19:2867. |
| [12] | 蔡雁兵,王志宏,张国珍,聂祚仁.Al2O3-TiC复合材料放电等离子烧结（SPS）致密化研究[J].北京工业大学学报,2003(01):112-115. |
| [13] | 司为民;郑灵仪;李鹏兴 et al.[J].复合材料学报,1995,12(01):68. |
| [14] | 梁英教;车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1993 |
| [15] | 贺文雄,李小强,胡连喜,王尔德.机械球磨对Ti-Al复合粉扩散反应的影响[J].材料科学与工艺,2000(04):26-29. |
| [16] | 王素梅,孙康宁,卢志华,李春胜,赵天平.Ti-Al/TiC陶瓷基复合材料烧结过程的研究[J].材料科学与工程学报,2003(04):565-568. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%