由于Cr(Ⅵ)对环境有不利影响,因此寻找不合Cr(Ⅵ)的钝化液非常重要.研究在连续热浸镀锌钝化液中以Cr(Ⅲ)、铈、钴替代Cr(Ⅵ),钝化液通过辊涂和烘干处理工艺得到钝化膜.试验通过电化学方法研究钝化膜的抗腐蚀行为.SEM形貌观察发现,所获得的钝化膜较Cr(Ⅵ)钝化膜具有更加致密的表面膜层,SiO2在膜层结构中阻碍了微裂纹的扩展,提高了膜层抗形变性能;电化学极化曲线研究表明,铈、钴抑制了阳极极化腐蚀过程;盐雾试验结果表明,复合钝化膜较传统钝化膜具有更好的抗蚀性能.钝化膜的膜附着量达70-80 mg/m2,试样出现锈蚀的时间可以达到192 h,试验色差为1.5.
参考文献
| [1] | De Stryeker J;Horzenberger F;Meert T.Cr-free thin organic coatings on galvanized steel sheet[A].Chicago:The Association for Iron & Steel Technology,2004:121-125. |
| [2] | Gabrielli C;Keddam M;Minouflet-Laurent F et al.Investigation of zinc chromatation Part Ⅱ.Electrochemical impedance techniques[J].Electrochimica Acta,2003,48:965. |
| [3] | Kendig M;Davenport A J;Isaacs H S .The Mechanism of Corrosion Inhibition by Chromate Conversion Coatings from X-Ray Absorption near Edge Spectroscopy (XANES) Corrosion[J].Science,1993,34:41-49. |
| [4] | Spencer L F.Conversion Coating[J].Metal Finishing,1966(01):57. |
| [5] | Eppensteiner F W;Jenkins M R.Chromate Conversion Coatings[J].Metal Finishing,1975(09):29. |
| [6] | 卢燕平,屈祖玉,任玉苓.耐指纹板表面黑变缺陷的研究[J].钢铁研究学报,2001(02):44-49. |
| [7] | 王君龙,梁国正,祝保林.纳米SiO2对氰酸酯树脂的增韧改性研究[J].宇航学报,2006(04):745-750. |
| [8] | 姚素薇,王小燕,张卫国,王宏智.纳米SiO2对聚氨酯清漆性能的影响[J].功能材料,2006(02):292-294. |
| [9] | 龙晋明,韩夏云,杨宁,郭忠诚.锌和镀锌钢的稀土表面改性[J].稀土,2003(05):52-56. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%