The friction stir weldabilities of the strain-hardened AA1050-H24 and precipitate-hardened AA6061-T6 aluminum alloys were examined to reveal the effects of material properties on the friction stir welding behavior. The experimental results are obtlained. (1) For AA1050-H24, the weld can possess smoother surface ripples; there is no elliptical weld nugget in the weld; there is no discernible interface between the stir zone and the thermomechanically affected zone;and the internal defect of the weld looks like a long crack and is located in the lower part of the weld. (2) For AA6061-T6, the weld usually possesses slightly rougher surface ripples; an elliptical weld nugget clearly exists in the weld; there are discernible interfaces among the weld nugget, thermomechanically affected zone and heat affected zone; and the internal defect of the weld is similar to that of the AA1050-H24 weld. (3) The effective range of welding parameters for AA1050-H24 is narrow, while the one for AA6061-T6 is very wide. (4) The maximum tensile strength efficiency of the AA1050-H24 joints is similar to that of the AA6061-T6 joints, i.e. 79% and 77%, respectively.
参考文献
| [1] | H Okamula;K Aota;M Ezumi .[J].Japanese Journal of Institute of Light Metals(Japan),2000,50:166. |
| [2] | W M Thomas;E D Nicholas;J.C.Needham;M.G.Murch, P.Temple-Smith C.J.Dawes .International Patent Application PCT/GB92/02203 and GB Patent Application 9125978.8[P].UK Patent Office London,1991. |
| [3] | K.E.Knipstrom;B.Pekkari .[J].Welding Journal,1997,76:55. |
| [4] | C.J.Dawes;W.M.Thomas .[J].Welding Journal,1996,75:41. |
| [5] | G.Campbell;T.Stotler .[J].Welding Journal,1999,78:45. |
| [6] | M R Johnsen .[J].Welding Journal,1999,78:35. |
| [7] | M Kumagai;S Tanaka .in Proc. 1st Int. Friction Stir Welding Symp[R].California USA Paper No. S3-P2,1999. |
| [8] | H Okamura;K Aota;M Sakamoto;M.Ezumi K.Ikeuchi .[J].Q J Jpn Welding Sci,2001,19:446. |
| [9] | Y Nagano;S Jogan;T.Hashimoto .in Proc. 3rd Int.Friction Stir Welding Symp[R].Kobe Japan Paper No. Post-12,2001. |
| [10] | Y S Sato;H Kokawa;M.Enomoto;S.Jogan .Metall.Mater[J].Transactions A,1999,30:2429. |
| [11] | Y S Sato;H Kokawa;M Enomoto;S.Jogan T.Hashimoto .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1999,30:3125. |
| [12] | Y S Sato;H Kokawa .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2001,32:3023. |
| [13] | J Hagstrom;R Sandstrom .[J].Science and Technology of Welding and Joining,1997,2:199. |
| [14] | L.-E.Svensson;L.Karlsson .Microstructure and mechanical properties of friction stir welded aluminium alloys with special reference to AA 5083 and AA 6082[J].Science and Technology of Welding and Joining,2000(5):285-296. |
| [15] | Y S Sato;M Urata;H Kokawa;K Ikeda.[A].Kobe Japan,2001:633. |
| [16] | Y.S.Sato;M.Urata;H.Kokawa;K.Ikeda M.Enomoto .[J].Scripta Materialia,2001,45:109. |
| [17] | O.V.Flores;C.Kennedy;L.E.Murr;D.Brown, S.Pappu, B.M.Nowak J.C.Mcclure .[J].Scripta Materialia,1998,38:703. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%