采用在低温煅烧过的磷石膏中加入缓凝剂和发泡剂的方法制备轻质墙体材料,研究了缓凝剂、水灰比和发泡剂对磷石膏试块强度和轻质化的影响.力学实验测试表明:缓凝剂掺量0.1％、水灰比0.65、发泡剂掺量0.02％的工艺下,磷石膏试块7d的抗压强度为4.6MPa,抗折强度为2.2 MPa,初凝时间为27 min,体积密度为0.82g/cm3;扫描电镜分析表明:此工艺下的磷石膏试块中孔隙合格且结晶质量良好.
参考文献
| [1] | Singh M .Role of phosphogypsum impurities or strength and microtrucyure of selenite plaster[J].Constr Build Materi,2005,19(06):480-486. |
| [2] | 张永志.重视磷石膏的综合利用促进磷肥工业可持续发展[J].磷肥与复肥,2009(02):11-13. |
| [3] | 侍昆,程麟,冯皓,陈丹,侯娟君.未预处理磷石膏砖的研究[J].硅酸盐通报,2010(06):1407-1411,1420. |
| [4] | 袁伟,谭克锋.磷石膏胶结料体系优化配制研究[J].硅酸盐通报,2009(02):341-345. |
| [5] | 杜采颐,严云,胡志华,谢晓丽,王素娟.利用磷石膏制备轻质材料初探[J].建筑材料学报,2008(03):353-358. |
| [6] | 刘代俊,刘玉琨,钟本和,杨三可,胡厚美,姚必新,番廷飚.高强度磷石膏砌块的研制[J].磷肥与复肥,2004(01):64-65. |
| [7] | Nurhayat Degirmenci .Utilization of phosphogypsum as raw and calcined material in manufacturing of building products[J].Construction and Building Materials,2008(8):1857-1862. |
| [8] | Sjngh M.;Garg M. .Making of anhydrite cement from waste gypsum[J].Cement and Concrete Research,2000(4):571-577. |
| [9] | I. Akin Altun;Yesim Sert .Utilization of weathered phosphogypsum as set retarder in Portland cement[J].Cement and Concrete Research,2004(4):677-680. |
| [10] | 彭家惠,陈明凤,瞿金东,张建新.柠檬酸对建筑石膏水化的影响及其机理研究[J].建筑材料学报,2005(01):94-99. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%