轮磨法测试铝及铝合金阳极氧化膜的耐磨性有其独特的优点.通过比较国内外测试方法标准,讨论了需要改进完善的几个方面,以为下一步我国标准修订提供参考.
参考文献
[1] | 朱祖芳.铝合金阳极氧化工艺技术应用手册[M].北京:冶金工业出版社,2007 |
[2] | GB/T 12967.2-1991.GB/T 12967.2-1991.铝及铝合金阳极氧化--用轮式磨损试验仪测定阳极氧化膜的耐磨性和磨损系数[S]. |
[3] | EN 12373-9-1998.EN 12373-9-1998.Aluminium and aIuminium aUoysanodizing-Part 9:measurement of wear resistance and wear index of anodic oxide coatings using an abrasive wheel wear test apparatus[S]. |
[4] | Iso 8251-1987.Iso 8251-1987.Anodized ahminium and aluminium alloys-Measurement of wear resistance and wear index of anodic oxide coatingswith an abrasive wheel wear test apparatus[S]. |
[5] | JIS H 8682-1-1999.JIS H 8682-1-1999.Test methods for abrasion resistance of anodlc oxide coatings on aluminium and ahminium alloysPart 1:wheel wear test[S]. |
[6] | GB/T 8014.2-2005.GB/T 8014.2-2005.铝及铝合金阳极氧化氧化膜厚度的测量方法第2部分:质量损失法[S]. |
[7] | GB/T 6462-2005.GB/T 6462-2005.金属和氧化物覆盖层厚度测量显微镜法[S]. |
[8] | GB/T 4957-2003.GB/T 4957-2003.非磁性基体金属上非导电覆盖层覆盖层厚度测量涡流法[S]. |
[9] | 北京矿冶研究总院分析室.矿石及有色金属分析手册[M].北京:冶金工业出版社,1990 |
[10] | GB/T 11109-1989.GB/T 11109-1989.铝及铝合金阳极氧化术语[S]. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%